Abstract:In this study, the recycled Al-Mg-Mn-Fe alloys having different Fe levels (0.1%, 0.5%, and 0.8%) were successfully developed by applying squeeze casting without heat treatment. Optical and scanning electron microscopy, synchrotron X-ray tomography and radiography, X-ray diffraction, and tensile tests combined with thermodynamic calculations were used to study the correlation between the microstructural evolution and mechanical properties. The results showed that for the alloys with an applied pressure of 75 MPa, as the Fe increase from 0.1% to 0.8%, the yield strength (YS), and ultimate tensile strength (UTS) increased from 122 MPa and 244–146 MPa and 289 MPa, and elongation decreased from 34% to 12%. Even though Fe additions increased the volume fraction of Fe-rich intermetallic phases, it significantly increased the UTS and YS. The synchrotron X-ray tomography and deep-etched results both show that the 3D morphology changed from individual Chinese-script to interconnected plate-like. The 3D morphology of 0.8Fe alloy clearly demonstrate that the hole partially or whole penetrated the entire rectangle-shaped Al6(FeMn) phases, which is due to the close-packed plane growth. In-situ synchrotron X-ray radiography results showed the facet growth behaviour of Al6(FeMn) in 0.8Fe alloys during solidification with a long needle-like shape. The size of primary Al6(FeMn) phases decreases, whereas their number increases with increasing cooling rate. Moreover, the applied pressure was beneficial in refining the size of α-Al grains and Fe-rich phases and reducing the volume fraction of pores, thus contributing to the improvement of strength and elongation. The in-situ tensile test results indicated that the crack initiated in the Fe-rich phases and pores, and the slip lines were blocked by the Fe-rich phases resulting in the strengthening of the secondary phases.

Influence of Fe-rich Particles on Microstructure Evolution, Texture and Mechanical Properties of Al–Mg–Si–Cu Alloys

Effect of Alloying Elements and Processing Parameters on Microstructure and Properties of 1XXX Aluminium Alloys

Revealing the influence of Fe on Fe-rich phases formation and mechanical properties of cast Al-Mg-Mn-Fe alloys

Effects of Cu Addition on the Microstructure and Properties of the Al–Mn–Fe–Si Alloy

Towards high mechanical performance Al–Cu–Mg–Fe–Ni alloy: influence of composition, solution treatment and aged process on microstructural evolution and mechanical properties

Multi-scale iron-rich phases induce fine microstructures in Al-Zn-Mg-Cu-Fe alloys

Effect of ultrasonic melt processing and cooling rate on microstructure evolution of Al–Cu–Mn–Mg–Fe–Si alloy

Effect of Initial Fe Content on Microstructure and Mechanical Properties of Recycled Al-7.0Si-Fe-Mn Alloys with Constant Mn/Fe Ratio

Effect of Al7Cu2Fe Particles on the Anisotropic Mechanical Properties and Formability of Al-Zn-Mg-Cu-Based Alloy Sheets

Effects of Fe content on microstructure and properties of Cu–Fe alloy

Effect of Si on Fe-rich intermetallic formation and mechanical properties of heattreated Al-Cu-Mn-Fe alloys

Synchrotron X-ray tomography investigation of 3D morphology of intermetallic phases and pores and their effect on the mechanical properties of cast Al-Cu alloys

The Dependence of Final Microstructure, Texture Evolution and Mechanical Properties of Al–Mg–Si–Cu Alloy Sheets on the Intermediate Annealing

Fe-bearing phase formation, microstructure evolution, and mechanical properties of Al-Mg-Si-Fe alloy fabricated by the twin-roll casting process

Fe content influence on the microstructure of solution-treated Sm-Co-Fe-Cu-Zr alloys

Influence of Fe and Mn on the Microstructure Formation in 5xxx Alloys-Part II: Evolution of Grain Size and Texture

Investigation of particles on the microstructure, texture and formability of Al–Mg-Si-Zn alloy for automotive body sheet

Relationship among solution heating rate, mechanical properties, microstructure and texture of Al−Mg−Si−Cu alloy

Influences of Fe Content and Cold Drawing Strain on the Microstructure and Properties of Powder Metallurgy Cu-Fe Alloy Wire

Evolution behavior of Fe and Fe-rich phases in high-Fe concentration Al-Si-Mg alloy with Mn, Cr, and Co alloyed

Effects of Fe addition on the microstructures and mechanical properties of as-extruded Zn-0.2Mg alloys