Abstract:Hot compression tests are carried out at temperatures ranging from 900 °C to 1050 °C, strain rates ranging from 0.001s−1 to 1s−1 and deformation degree ranging from 60% to 70% on the Gleeble-3500 thermal simulator. Strain-compensated Arrhenius constitutive model, activation energy maps, hot processing maps and microstructure evolution are used to analyse the flow behavior of as-cast Ti-55511 alloy. At low temperature (≤950 °C), the flow softening behavior is mainly related to cracks, deformation bands (DBs) and DRV at high temperature (≥1000 °C) and high strain rate (≥0.1s−1), and DRV at high temperature (≥1000 °C) and low strain rate (≤0.01s−1). DBs and cracks are the main forms of hot deformation instability. There is a competitive relationship between DRV and DBs. Under high strain rate (≥0.1s−1), DBs are more likely to occur. Under low strain rate (<0.1s−1), the DBs are restrained by DRV. The simultaneous activation of different slip systems causes the rotation of different areas in the grains to form DBs. The DRX grains in the DBs are produced by continuous dynamic recrystallization (CDRX) and discontinuous dynamic recrystallization (DDRX), but the DRX grains in the sample without DBs are produced by CDRX. The analysis of hot activation energy (Q), strain rate sensitivity index (m), power dissipation efficiency (η), flow instability parameter (ξ(ε˙)) and microstructure analysis showed that 1000°C–1050 °C/0.001s−1–0.01s−1 are an optional processing window. And the proportion of recrystallization is the highest at strain of 1.2 and 1000 °C/0.01s−1, so it can be considered as the optimal processing parameter.

Optimization of Forging Process Parameters of Ti600 Alloy by Using Processing Map

Characterization of high-temperature deformation behavior of as-cast Ti60 titanium alloy using processing map

Optimization of hot deformation parameters for multi-directional forging of Ti65 alloy based on the integration of processing maps and finite element method

Optimization of Hot Process Parameters of Ti–6.7Al–2Sn–2.2Zr–2.1Mo–1W–0.2Si Alloy with Lamellar Starting Microstructure Based on the Processing Map

Research on the Hot Deformation Behavior of Ti40 Alloy Using Processing Map

Hot Deformation Behavior and Processing Maps of Ti-1300 Alloy

High temperature deformation behavior of a near alpha Ti600 titanium alloy

Characterization of hot deformation behavior of as-cast TC21 titanium alloy using processing map

Processing Map of One Kind of Metastable Β Titanium Alloy

Constitutive Model and Microstructure Evolution of a Novel TG6 High-Temperature Titanium Alloy during Hot Deformation

Revealing Hot Deformation Behavior and Optimizing Process Parameters of As-Cast Ti–5Al–5Mo–5V–1Cr–1Fe Alloy

Hot deformation behavior and process parameters optimization of Ti–6Al–7Nb alloy using constitutive modeling and 3D processing map

Flow Behavior and Processing Map for Hot Deformation of ATI425 Titanium Alloy

High Temperature Deformation Behavior of Ti–46Al–2Cr–4Nb–0.2Y Alloy

Understanding processing map and microstructural evolution of powder metallurgy Ti-6Al-4V within a wide range of deformation temperatures

The High-Temperature Deformation Behavior of a Novel Near-Α Titanium Alloy and Hot-Forging Based on the Processing Map

Characterization of Hot Processing Parameters of Powder Metallurgy TiAl-based Alloy Based on the Activation Energy Map and Processing Map

Characterization of the Hot Deformation Behavior of a Ti–22Al–25Nb Alloy Using Processing Maps Based on the Murty Criterion

Softening mechanism and process parameters optimization of Ti-4.2Al-0.005B titanium alloy during hot deformation

Hot Deformation and Processing Maps of Low Cost Ti-Al-V-Fe-O Alloy

Hot Deformation and Processing Map of Ti-46Al-2Cr-4Nb-Y Alloy