Effect of Zn Addition on the Microstructures and Mechanical Behaviors of As-cast Mg-2.5Y-1Ce-0.5Mn Alloy

Xiaoru Zhang,Guixun Sun,Jiaan Liu,Chaojie Che,Mengli Yang,Shuang Han,Daqing Fang,Zhonghao Jiang,Jianshe Lian

DOI: https://doi.org/10.1088/2053-1591/ab66f8

IF: 2.025

2020-01-01

Materials Research Express

Abstract:The effect of Zn addition on the microstructures and mechanical behaviors of as-cast Mg-2.5Y-1Ce-0.5Mn alloy was investigated. Microstructure observation demonstrated that with the addition of 1wt%, 3wt% and 5wt% Zn, the ternary phases of LPSO phase, LPSO phase +W-phase and W-phase +T-phase (Mg-Zn-Ce) are precipitated orderly, and the volume fraction of eutectic phases increases. The results of tensile tests demonstrated that with increasing Zn addition, the yield strength sigma increase nonlinearly. Based on the analysis of microstructure, nanoindentation results and deformation surfaces, it found that the sigma Y S delta in 1wt% Zn alloy is contributed from the LPSO phase with an excellent plastic accommodation while the insufficient accommodated role of LPSO phase and the easily broken W-phase deteriorate the ductility of 3wt% Zn alloy. The hard and brittle T-phase also damages the ductility, while the fine grains contribute to the moderate elongation in 5wt% Zn alloy. The mainly arises from a sustainable increase of strain hardening ability after yielding that associated with both the high yielding point and excellent ductility.