Critical Field Analysis and Magnetocaloric Effect of A-Site Double-Doped Manganese Oxide La0.9EuSr0.1MnO3
Hongwei Chen,Cheng Li,Jianjun Zhao,Yi Lu,Fengze Cao,Wenxing Wang,Lin Zheng,Xiang Jin
DOI: https://doi.org/10.1007/s10948-021-05945-4
2021-06-28
Journal of Superconductivity and Novel Magnetism
Abstract:Polycrystalline La0.9-xEuxSr0.1MnO3 (x = 0.000, 0.025) samples were prepared using a traditional high temperature solid-state reaction method. The effects of double doping of cationic Eu3+ and Sr2+ on the preformed clusters, critical field behavior, and change of magnetic entropy of LaMnO3 were studied systematically. The results show that polycrystalline La0.9-xEuxSr0.1MnO3 (x = 0.000, 0.025) samples are orthogonal crystal structures with a good unidirectionality and the space group of the polycrystalline samples is Pbnm. As the temperature increased from 15 to 380 K, the polycrystalline La0.9-xEuxSr0.1MnO3 (x = 0.000, 0.025) sequentially displayed the characteristics of cluster spin glass, ferromagnetic phase, preformed cluster, and paramagnetic phase. For both La0.9-xEuxSr0.1MnO3 samples, the second-order phase transition occurs near Curie temperature. The critical index of the undoped parent compound and doped sample fitted best to the mean-field model and 3D-Heisenberg model, respectively. At an applied magnetic field of 7 T, the maximum absolute values of the magnetic entropy changes of the two samples were 2.76 ± 0.002 J·kg−1·K−1 and 2.81 ± 0.002 J· kg−1· K−1, respectively, and the temperature corresponding to the maximum absolute values of the magnetic entropy change was approximately 130 K. The magnetic refrigerant capacities (RC) of the two La0.9-xEuxSr0.1MnO3 samples were 436.01 ± 0.002 J· kg−1 and 438.09 ± 0.002 J· kg−1, respectively. Our results revealed that the changes in magnetic entropy and magnetic refrigerating capacity of the doped sample increased compared to the parent sample, suggesting that the double-doped manganese oxide La0.9-xEuxSr0.1MnO3 samples can be used as magnetic refrigerants in the medium temperature range of 80 to 250 K.
physics, condensed matter, applied