SrFe(1-x)MoxO(2+delta): parasitic ferromagnetism in an infinite-layer iron oxide with defect structures induced by interlayer oxygen

Jianhui Guo,Lei Shi,Jiyin Zhao,Yang Wang,Xueyou Yuan,Yang Li,Liang Wu

DOI: https://doi.org/10.1088/2053-1591/aabbed

IF: 2.025

2018-01-01

Materials Research Express

Abstract:The recent discovered compound SrFeO2 is an infinite-layer-structure iron oxide with unusual square-planar coordination of Fe2+ ions. In this study, SrFe1-xMoxO2+delta (x < 0.12) is obtained by crystal transformation from SrFe1-xMoxO3-delta perovskite via low-temperature (<= 380 degrees C) topotactic reduction. The parasitic ferromagnetism of the compound and its relationship to the defect structures are investigated. It is found that substitution of high-valent Mo6+ for Fe2+ results in excess oxygen anions O2- inserted at the interlayer sites for charge compensation, which further causes large atomic displacements along the c-axis. Due to the robust but flexible Fe-O-Fe framework, the samples are well crystallized within the ab-plane, but are significantly poorer crystallized along the c-axis. Defect structures including local lattice distortions and edge dislocations responsible for the lowered crystallinity are observed by high resolution transmission electron microscopy. Both the magnetic measurements and electron spin resonance spectra provide the evidence of a parasitic ferromagnetism (FM). The week FM interaction originated from the imperfect antiferromagnetic (AFM) ordering could be ascribed to the introduction of uncompensated magnetic moments due to substitution of Mo6+ (S = 0) for Fe2+ (S = 2) and the canted/frustrated spins resulted from defect structures.