Molecular Orientation and Phase-Transition Behavior of Langmuir-Blodgett and Casting Films of Reversed Duckweed Polymer Es-1 Studied by Infrared Spectroscopy

Q Wang,B Zhao,X Zhang,Jc Shen,Y Ozaki

DOI: https://doi.org/10.1021/la020608g

IF: 3.9

2002-01-01

Langmuir

Abstract:A kind of amphiphilic polymer, ES-1, is transferred onto solid substrates as so-called "reversed duckweed" polymeric Langmuir-Blodgett (LB) films. Their orientations, structures, and phase-transition behaviors were studied in detail by infrared (IR) transmission and reflection-absorption (RA) spectroscopy. The IR studies have revealed that the alkyl chains are nearly perpendicular-to the film surface and assume highly ordered conformation. The first monolayer has a different orientation and arrangement from other layers in a multilayer ES-1 LB film deposited on a Au-evaporated glass slide because of the interaction between the gold surface and hydrophilic headgroup of ES-1. IR-RA spectra of an ES-1 LB film on a Au-evaporated glass slide at evaporated temperatures have shown that the order-disorder phase transition of the LB film takes place at about 60 degreesC after the clear pretransitional alterations. The packing density of alkyl chains decreases gradually with temperature after the order-disorder transitions in the LB films. The alkyl chains in ES-1 casting films on a CaF2 plate and a Au-evaporated glass slide are tilted considerably. The studies on the phase-transition behavior have revealed that the two casting films give rise to the order-disorder transition at about 75 degreesC after undergoing the pretransitional changes. For the casting film of ES-1 on the Au-evaporated glass slide, there is a phenomenon of reorientation that the alkyl chains change from more tilted orientation at room temperature to more perpendicular orientation at higher temperature before, the order-disorder transition takes place and turn tilted again above the transition temperature.