Effects of Charge Compensators on Structure and Luminescent Properties of CaAl2Si2O8∶Eu3+phosphors
WANG Fei,TIAN Yiguang,ZHANG Qiao
DOI: https://doi.org/10.3969/j.issn.1004-244x.2014.06.025
2014-01-01
Abstract:A series of red phosphors CaAl2Si2O8∶Eu3+,R+(R=Li,Na,K)were prepared by high temperature solid?state reaction. Influence of charge?compensator R+on structure and luminescence properties of the CaAl2Si2O8∶Eu3+was studied. The CaAl2Si2O8∶Eu3+,R+(R= Li,Na,K)red phosphors have the same crystal structure as that of the CaAl2Si2O8,both of them belong to triclinic system,and P?1 space group. Doping with the charge?compensators(Li+,Na+,or K+)has little effect on the crystal structure of the matrix. The excitation spectra are composed of a broad excitation band located at 220 to 580 nm and a group of sharp peaks. The emission spectra are located at 594 to 615 nm,and present a number of sharp lines emission. The emission peak at 594 nm is attributed to 5D0?7F1 magnetic dipole transition of the Eu3+,while the peak at 615 nm is because of 5D0?7F2 electric dipole transition of the Eu3+. The emission spectrum intensity of the CaAl2Si2O8∶Eu3+,R+(R=Li,Na,K)firstly increases with increasing charge?compensator concentration,then decreases with it. The optimal doping concentration of the Li+,Na+and K+is 0.04,0.03 and 0.03,respectively. And the corresponding improvement in the emission intensity is 138.53%,85.44%and 48.35%. Therefore,the Li+is the most effective charge?compensator.