Abstract:Unraveling the varied modification mechanisms of trace elements under diverse cooling rates is of great importance to regulate the morphology of primary Mg 2 Si in hypereutectic Al-Mg 2 Si alloys. In the present work, the modification mechanisms of Sr and Sb in Al-20Mg 2 Si alloys under different cooling rates are discussed in detail. Increasing the cooling rates from ~ 50 to 76 °C/s to ~ 213 to 230 °C/s leads to the morphology transition of primary Mg 2 Si from hoppers to dendrites, which is attributed to a smaller constitutional zone with the increase of temperature gradients introduced by high cooling rates. The addition of 0.15 wt pct Sr modifies the morphology of primary Mg 2 Si phase to cubes at cooling rates of ~ 50 to 76 °C/s and ~ 213 to 230 °C/s with the same modification mechanism, i.e. , by increasing nucleation driving force for primary Mg 2 Si and the adsorption-poisoning effect. In contrast, the modification mechanisms of Sb are different under varying cooling rates. At low cooling rates of ~ 50 to 76 °C/s, Sb modifies the morphology of primary Mg 2 Si to be truncated octahedrons by introducing Mg 3 Sb 2 particles as heterogeneous nuclei and the substitution of Sb to Si in Mg 2 Si crystals. At high cooling rates of ~ 213 to 230 °C/s, primary Mg 2 Si grows coarser with a dendrite morphology due to solute trapping, which changes the modification mechanism to substitution alone. Moreover, it is interesting that at cooling rates of ~ 213 to 230 °C/s, primary and eutectic Mg 2 Si particles in the Al-20Mg 2 Si-0.15Sr alloy are refined simultaneously, which greatly suppresses the crack formation and propagation. Accordingly, the ultimate tensile strength and elongation to failure are increased to ~ 242 MPa and ~ 5.6 pct compared to the unmodified alloy (~ 188 MPa and ~ 1.4 pct, respectively).

Modification and Refinement Mechanism of Mg2Si Phase in Srcontaining AZ61-0.7Si Magnesium Alloy

Comparison of Sb and Sr on Modification and Refinement of Mg 2 Si Phase in AZ61-0.7Si Magnesium Alloy

Effects of Sr on the Microstructure, Tensile and Creep Properties of AZ61-0.7Si Magnesium Alloy

Comparison about effects of Sb, Sn and Sr on as-cast microstructure and mechanical properties of AZ61–0.7Si magnesium alloy

As-cast microstructure and mechanical properties of Sr and Sb modified Az61-0.7Si magnesium alloy

Microstructure Refinement and Mechanical Properties of Eutectic Mg2Si Reinforced Mg Matrix Composites Containing Sr Element

As Cast Microstructure and Mechanical Properties of Mg–6Al–1Zn–0·7Si Magnesium Alloys Modified by Sn and Sr Additions

Effects of Sr on Microstructure and Mechanical Properties of Mg-9al-1si-0.3zn Alloy

Effect of Si, Sr Additions on Microstructure and Mechanical Properties of AZ91 Alloy

Effect of Strontium Addition on Silicon Phase and Mechanical Properties of Zn–27Al–3Si Alloy

Effect of Sr and Nd on Microstructure and Mechanical Properties of AZ91-1Si Alloy

Effect of Strontium on the Microstructure, Mechanical Properties, and Fracture Behavior of AZ31 Magnesium Alloy

Effects of Sr on Microstructure and Mechanical Properties of AZ31 Magnesium Alloy

The Effect of Sr Modification on the Microstructure and Properties of Mg2si Reinforced Near- Eutectic Al-Si Alloy

Effect of Sr addition on the grain refinement of AZ31 magnesium alloys

As-cast Microstructure and Sr-containing Phases of AZ31 Magnesium Alloys with High Sr Contents

The influences of Sr on the microstructure and mechanical properties of Mg-5Zn-2Al alloy

Effect of Sr Addition on the Microstructure and the Properties of AZ91 Magnesium Alloy

An investigation of second phases in as-cast AZ31 magnesium alloys with different Sr contents

Varied Modification Mechanisms of Sr and Sb under Diverse Cooling Rates on Primary Mg 2 Si in an Al-20Mg 2 Si Alloy

Effects of Sr on the As-cast Microstructure of Mg-3Al-1Zn Magnesium Alloy