Abstract:In the research experiments on the early growth characteristics of BaMoO4 thin film deposited by constant-current electrochemical technique, some important experimental phenomena were discovered. They are mainly as follows; the crystalline nucleuses formed at the initial stage of the film growth possess the skeleton of the scheelite-structure; the crystalline nucleuses and the crystal granules which are just growing up are all porous, and the crystalline granules have the interstices of the beehive form obviously; along with the increase of growing time, the porous degree of the scheelite-structure framework is dieing down gradually, and the crystal line granules tend to become full and the surfaces of the crystalline granules tend to become smooth for certain time; and the crystalline nucleuses that are just growing up also have the similar characteristic in the process of film growth. From the growing mechanism analysis of BaMoO4 thin film prepared by electrochemical technique, it is considered that at the early stage of film growth the Mo atoms of the substrate make up the polyhedron growth units with the form of [MoO4]2- through electrochemical reaction; the places where these units pile up and grow prior are those of the defects at the substrate to form the crystalline nucleus with scheelite-structure, and then the growth units combine with [Ba]2+ in solution to synthesize BaMoO4 crystalline granules, and afterwards the granules grow up gradually. Obviously, these findings will enrich the knowledge of crystal growth dynamics and conduct the experiments of thin film growth by using electrochemical technique.

Growth of High Quality and Large-Sized Rb0.3MoO3 Single Crystals by Molten Salt Electrolysis Method

Growth of red bronze K0.33MoO3 single crystals

Growth of Single Crystals of Bismuth Molybdenum Oxides

Single crystal Tl0.3MoO3 growth by electrolytic reduction method of a Tl2CO3–MoO3 melts

Flux Growth and Characterization of SrMo0.93O3 Single Crystal

Growth Of Bi2sr2cacu2o8 Single-Crystals From Bi-Rich Melts

Single Crystal T0.3moo3 Growth By Electrolytic Reduction Method Of A T1(2)Co(3)-Moo3 Melts

Crystal Growth of Rare Earth-Transition Metal Borocarbides and Silicides

Crystal growth and thermal properties of a LiY(MoO 4 ) 2 crystal

Experimental researches on the growth unit of BaMoO4 thin film deposited by electrochemical method

Low-Temperature Synthesis of Large-Scale Single-Crystal Molybdenum Trioxide (moo3) Nanobelts

Molten salt synthesis and characterization of large size β-Mn2V2O7 with single crystal character

Crystal-Growth And Characterization Of Rb0.3k0.7tiopo4

Study of Growth Units and the Growth Habit of Pbmoo4 Crystal Using High Temperature Raman Spectra

Single-crystal Growth and Physical Properties of 50% Electron-Doped Rhodate Sr1.5La0.5RhO4

Growth of Lead Molybdate Crystals by Vertical Bridgman Method

Growth and Characterizations of La2CaB10O19 Crystal from the New Li2B4O7−MoO3 Flux System with Lower Volatility and Viscosity

Crystal Growth of Quasi-Two-dimensional Purple Bronze KxMo6O17

Multiferroic Properties of Single-Crystalline Bi0.8La0.2FeO3 Microsized Particles Synthesized by Molten Salt Method

Crystal growth and physical properties of ternary bismuth molybdenum oxides Bi x MoO y ( x =0.21, 0.25; y =3 + δ)

Experimental Researches on the Growth Characteristics of SrMoO4 Thin Film Prepared by Electrochemical Technique