Hydrothermal synthesis of (Zr,U)SiO4, an efficient pathway to incorporate uranium in zircon
Paul Estevenon,Thomas Barral,Arthur Avallone,Mateo Jeffredo,Alexis De La Hos,Andrew Strzelecki,Xavier F Le Goff,Stéphanie Szenknect,Kristina O. Kvashnina,Philippe Moisy,Renaud Podor,Xiaofeng Guo,Nicolas Dacheux
DOI: https://doi.org/10.1039/d4dt01604a
IF: 4
2024-07-26
Dalton Transactions
Abstract:The preparation of synthetic (Zr,U)SiO4 solid solution is a challenging operation, as the conventional high temperature solid state method limits the solubility of uranium (4 ± 1 mol.%). in the orthosilicate phase due to is thermodynamic instability. However, these compounds are of great interest as (Zr,U)SiO4 solid solutions with uranium contents exceeding this concentration, were observed in corium formed in nuclear accidents. It has been identified that hydrothermal synthesis pathways can be used for the formation of metastable phase, such as USiO4. The investigation carried out in this study has indeed allowed the formation of (Zr,U)SiO4 compounds with high uranium contents. It was found that (Zr,U)SiO4 forms a close to ideal solid solution with uranium loading up to 60 mol% using a hydrothermal treatment for 7 days at 250°C, at pH = 3 and starting from a equimolar reactants concentration equal to 0.2 mol·L‐1. Since most of the (Zr,U)SiO4 syntheses resulted in a mixture of silicate and oxide, a purification procedure was developed to obtain pure silicate compounds. After purification, these compounds were found to be stable up to 1000°C under an inert atmosphere (argon). The characterization methods used to explore the synthesis and thermal stability included powder X-ray diffraction (PXRD), Fourier transformed infrared (FTIR) and Raman spectroscopies, scanning electron microscopy (SEM) and thermogravimetric analysis (TGA).
chemistry, inorganic & nuclear