Wenhao Zhang,Jie Li,Shiwen Yi,Peng Zu,Jingxuan Wu,Jiawei Lin,Min Li,Wenrou Su
DOI: https://doi.org/10.1016/j.jallcom.2021.159563
IF: 6.2
2021-08-01
Journal of Alloys and Compounds
Abstract:The M-type Sr hexaferrites with nominal compositions Sr1−xLaxNbxFe12−xO19(x = 0.00, 0.04, 0.08, 0.12, 0.16, 0.20) were fabricated by solid-state reaction method. The microstructure and magnetic properties of hexaferrites were characterized by X-ray diffraction (XRD), Fourier transformer infrared (FTIR) spectroscopy, filed emission scanning electron microscopy (FE-SEM) and vibrating sample magnetometer (VSM). The regular changes of microstructure and magnetic properties were studied at 1300 °C by doping quantity. XRD results show that the substitution of La-Nb is successful when x < 0.16, and α-Fe2O3 begins to appear when x > 0.16; FT-IR shows that there are frequency bands of tetrahedral and octahedral Fe‒O at 613 cm−1 and 451 cm−1, which proves the formation of lattice and structure of M-type Sr1−xLaxNbxFe12−xO19 hexagonal ferrite respectively; The SEM micrographs are regular hexagonal block with tight arrangement and obvious layering. EDS indicates that all elements are predetermined and no other elements are produced. VSM shows that the sample obtains high saturation magnetization (M s ), and increases slightly with the increase of doping amount. The coercivity (H c ) first increases with Nd-Nb Zn content (x) from 0.00 to 0.04, and then decreases when Nd-Nb Zn content x > 0.08; the value of SQR, magnetic crystal anisotropy constant (k 1 ) and magnetic anisotropy field (H a ) decrease with the increase of doping amount, and the number of magnetons (n B ) is consistent with the saturation magnetization (M s ). In this paper, for the first time we have studied the mechanism of La-Nb co-substituted which will lead to the change of ferrite morphology and properties at high temperature.
materials science, multidisciplinary,chemistry, physical,metallurgy & metallurgical engineering