Temperature-Modulated Growth of MOCVD-Derived YBa2Cu3O7−x Films on IBAD-MgO Templates
Fei Zhang,Jie Xiong,Ruipeng Zhao,Yan Xue,Hui Wang,Qiuliang Wang,Yuanying He,Pan Zhang,Bowan Tao
DOI: https://doi.org/10.1007/s10948-015-3101-y
2015-01-01
Journal of Superconductivity and Novel Magnetism
Abstract:Thecost-effective and environment-friendly template of LaMnO 3 /epi-MgO/ion beam-assisted deposited (IBAD-)MgO/solution deposition planarized (SDP) Y 2 O 3 /Hastelloy tape was used as the substrate, on which the technique of metal organic chemical vapor deposition (MOCVD) has been applied to depositing 1.2- μ m-thick YBa 2 Cu 3 O 7− x (YBCO) films by modulating the substrate temperature ranging from 750 to 850 ∘ C. The effects of substrate temperature on the preferential orientation, textures, surface morphology, and performance of the YBCO films were systematically investigated. X-ray diffraction and scanning electron microscope revealed that as substrate temperature increased from 750 to 810 ∘ C, the orientation of YBCO films was transferred from the a -axis to the c -axis; meanwhile, the textures were improved and the films became denser. However, as the substrate temperature rose above 810 ∘ C, the composition distributions and textures of YBCO films degraded quickly, and the films were barium-poor with CuYO 2 impurity arising, of which all negatively affected the critical current density ( J c ) of YBCO films. Around 810 ∘ C, the YBCO film was of the best crystallization and microstructure as well as highly epitaxial growth, leading to the highest J c of 1.8 MA/cm 2 at 77 K and self-field.