Electrical Transport Properties in La0.7Ca0.3-xSrxMnO3 Thin Films

Zhang Yuan-Yuan,Tang Xiao-Dong,Chen Ying,Wang Gen-Shui,Dong Xian-Lin

DOI: https://doi.org/10.15541/jim20150397

IF: 1.292

2016-01-01

Journal of Inorganic Materials

Abstract:The influence of the chemical composition on the structure, magnetic and electrical transport properties of La0.7Ca0.3-xSrxMnO3 (LCSMO, x <= 0.05) thin films was systematically studied. LCSMO thin films were prepared by Sol-Gel method. XRD results show that all the films have typical perovskite structure. With increase of Sr doping concentration, both Curie temperature T-C and metal-insulator transition temperature T-MI of LCSMO thin films increase monotonously. When Sr doping concentration x <= 0.05, with increase of temperature, absolute value of MR decreases first, then increases to a maximum value around T-MI, and finally decreases, which indicates that the disorder coming from phase separation around T-MI contributes greatly to MR. The field dependence of MR values at certain temperature can be classified into two kinds. When the temperature is much lower than T-MI, dual gradient of MR with the magnetic field is shown. The tunneling effect on the grain boundaries plays a dominant part in the low magnetic field, and this effect is particularly sensitive to the magnetic field; the suppression of spin fluctuations by magnetic field is the main reason in the high magnetic field range. When the temperature is higher than T-MI, MR of LCSMO thin films changes almost linearly with the magnetic field which is mainly due to suppression of spin fluctuations by magnetic field.