Abstract:The surface-modified activated carbon fibers (ACFs) with rich nitrogen-containing functional groups were prepared by heat-treatment of urea-loaded ACFs. Their nitrogen content, the surface property and the porosity were examined by element analysis, XPS, TGA and low temperature N-2 adsorption, and their SO2 removal performances were comparatively tested with the pristine ACF and the ACF merely heat-treated without urea-loading (ACF-H). The results revealed that the total nitrogen content of the surface-modified ACFs was much higher than that of the pristine ACFs. In particular, the content of pyridine nitrogen was found to be increased about 4.4 times. The specific surface area and the pore volume of the surface-modified sample were larger than those of the pristine ACF but smaller than those of the ACF-H. However, the surface-modified ACF exhibited a much improved SO2 removal activity. Its breakthrough SO2 capacity and SO2 removal efficiency at the stable stage of the desulfurization process increased 3.0 and 1.64 times, respectively, as compared with the ACF-H. The nitrogen-containing groups, particularly for the pyridinic nitrogen, rather than the developed pore structure should account for the excellent desulfurization activity of the surface-modified ACFs.

ENHANCEMENT OF CONTINUOUS REMOVAL OF SO2 ON SURFACE-MODIFIED ACTIVATED CARBON FIBERS BY NITROGEN-CONTAINING FUNCTIONAL GROUPS