Synthesis and Self-assembly of Poly(ethylene glyco1)-g-Poly(gamma-benzyl-L-glutamate) Rod-Coil Graft Copolymers
Shuo Zhang,Qing Li,Jia-ping Lin,Chun-hua Cai,Li-quan Wang
DOI: https://doi.org/10.11777/j.issn1000-3304.2017.16258
2017-01-01
Acta Polymerica Sinica
Abstract:Poly(ethylene glyco1)-g-poly(gamma-benzyl-L-glutamate) (PEG-g-PBLG) graft copolymers, bearing hydrophilic PEG backbone and hydrophobic PBLG side chain, were synthesized via ring opening polymerization of gamma-benzyl-L-glutamate-N-carboxyanhydride (BLG-NCA) using PEG-g-NH2 as the initiator. The molecular weight and polydispersity index of the graft copolymers as well as conformation of PBLG chains were characterized by proton nuclear magnetic resonance (H-1-NMR), gel permeation chromatography (GPC), and Fourier transform infrared spectrum (FTIR), respectively. Self-assemblies were prepared by a selective solvent method with tetrahydrofuran (THF) as the initial common solvent and water as the selective solvent. The critical water content (CWC) for the graft copolymer aggregation was determined by turbidity measurement (OD). The CWC value decreases from 17.3 wt% to 12.8 wt% gradually with the increase in PBLG length (the initial concentration is 0.5 g L-1). The morphologies and structures of the formed aggregates were investigated by scanning electron microscopy (SEM), transmission electron microscopy (TEM), atom force microscopy (AFM), and laser light scattering measurements (LLS). The results show that the graft copolymers are able to self-assemble into spherical compound micelles when the PBLG side chain is relatively short. As the PBLG length increases, the aggregates gradually transform to rod-like aggregates and vesicles. In addition to the experiments, the self-assembly of the graft copolymers was investigated using dissipative particle dynamics (DPD) simulation based on a coarse-grained coil-g-rod graft copolymer model. The simulation results were in agreement with the experimental findings, and additional information such as chain distribution of copolymers in aggregates was obtained. Besides, it was found that the initial polymer concentration affected the aggregate size but no significant influence was observed on the aggregate morphology. When prepared at higher initial polymer concentration (1.0 g L-1), the aggregates obtained were much larger in size and narrower in size distribution. Finally, based on both the experimental and the simulation results, a mechanism for the self-assembly of PEG-g-PBLG graft copolymers was proposed.