Abstract:Objectives: The incorporation of thiourethane-based oligomeric additives into resin composite formulations leads to improvement in mechanical properties and reduction in polymerization stress, but may increase viscosity. The objective of this study was to functionalize filler particle surfaces with thiourethane silane molecules and determine the impact of the inorganic filler loading and surface treatment on the behavior of experimental resin composites with systematically-varied organic matrices. Methods: Thiourethane oligomer was synthesized de novo, and grafted to the surface of 0.7um barium glass. BisGMA and TEGDMA (BT) were combined (at 30:70, 50:50 or 70:30 wt%) to 50 or 75 wt% of methacrylate (MA-Sil - control) or thiourethane-silanized (TU-Sil) particles. Composites were made polymerizable by the addition of 0.2 wt% BAPO and 0.05 wt% BHT was added as inhibitor. A mercury arc lamp (320-500 nm) at 800 mW/cm2 was used for all curing procedures. Kinetics of polymerization was assessed by near-IR spectroscopy in real time. Polymerization stress was determined with a cantilever system in real time (Bioman). Flexural modulus and strength were determined in 3-point bending (25x2x2 mm). Water sorption and solubility and film thickness were tested according to ISO 4049. Polymeric network characteristics were analyzed by dynamic mechanical analysis (DMA). Data was analyzed with two-way ANOVA/Tukey's test (95%). Results: Viscosity increased with the increase in BisGMA and/or filler amounts. Overall, TU-Sil containing composites showed delayed vitrification and higher final DC. Filler concentration did not affect DC neither flexural strength. DC decreased with increasing BisGMA content. Polymerization stress reduced and flexural modulus increased for higher filler content, especially for formulations containing TU-Sil particles. The water stability was positively affected by the increase in amount of BisGMA and inorganic filler particles. In terms of polymeric network, the addition of TU-Sil particles increased the Tg and decreased the E' and cross-link density. Conclusions: With the exception of flexural modulus, all tested properties were significantly impacted by the matrix viscosity and/or the addition of TU-Sil filler particles. In general, the use of thiourethane oligomers as a silane coupling agent was able to reinforce the materials and reduce the polymerization stress without negatively affecting the viscosity of the system.

Effect of filler surface-treatment on dynamic viscoelastic properties for PMVS/SiO2 composites

Preliminary Study on the Dynamic Properties of PMVS Filled with Surface-treated Silica

Effect of Filler Network on Dynamic Viscoelastic Properties of Uncured Polymethylvinylsiloxanes Filled with Silica and Carbon Black

Behavior of epoxy resin filled with nano-SiO<sub>2</sub> treated with a Eugenol epoxy silane

EFFECT OF SILANE COUPLING AGENTS ON DYNAMIC RHEOLOGICAL PROPERTIES FOR UNVULCANIZED SSBR/SILICA COMPOUNDS

The effects of filling method on silicone rubber composites filled with SiO2 and TiO2

DYNAMIC RHEOLOGICAL BEHAVIOR OF SSBR/SiO2 COMPOUNDS

Filler Effects on the Phase Separation Behavior of Poly (methyl Methacrylate)/poly (Styrene-Co-acrylonitrile) Binary Polymer Blends

Influence of Surface Property of CaCO3 Fillers on Apparent Viscosity of Filled Polydimethylsiloxane

Effects of Vinyl Functionalized Silica Particles on Thermal and Mechanical Properties of Liquid Silicone Rubber Nanocomposites

Dynamic rheological behavior of ssbr/si02 compounds

Novel experimental approach to evaluate silica–elastomer interactions of vulcanizates

Effect of size and content of mesoscopic fillers on the polymerization induced viscoelastic phase separation

Rheology of Fumed Silica/Polydimethylsiloxane Suspensions

Effect of silica particle size and filler content on the fracture properties of epoxy resin composite

Different Rheological Behaviors of Reinforced Poly(methylvinylsiloxane) by Mesoporous and Spherical Silica Microparticles

Influence of the organic matrix composition on the polymerization behavior and bulk properties of resin composites containing thiourethane-functionalized fillers

Influence of Incorporating CaCO3 into Room Temperature Vulcanized Silicone Sealant on Its Mechanical and Dynamic Rheological Properties

Viscoelastic Properties of Nanosilica‐filled Epoxy Composites Investigated by Dynamic Nanoindentation

Impact of Dispersion Processes and Surfactant on Performance of Silica-Silicone Nanocomposites

Effect of Mesoscopic Fillers on the Polymerization Induced Viscoelastic Phase Separation at Near- and Off-Critical Compositions.