Abstract:A coordination-assisted synthetic approach is reported here for the synthesis of highly active and stable gold nanoparticle catalysts in ordered mesoporous carbon materials using triblock copolymer F127 as a structure-directing agent, thiol-containing silane as a coordination agent, HAuCl4 as a gold source, and phenolic resin as a carbon source. Upon carbonization, the gold precursor becomes reduced to form monodispersed Au nanoparticles of ca. 9.0 nm, which are entrapped or confined by the "rigid" mesoporous carbonaceous framework. Nanoparticle aggregation is inhibited even at a high temperature of 600 degrees C. After removal of the silica component, the materials possess the ordered mesostructure, high surface area (similar to 1800 m(2)/g), large pore volume (similar to 1.19 cm(3)/g), and uniform bimodal mesopore size (<2.0 and 4.0 nm). The monodispersed gold nanoparticles are highly exposed because of the interpenetrated bimodal pores in the carbon framework, which exhibit excellent catalytic performance. A completely selective conversion of benzyl alcohol in water to benzoic acid can be achieved at 90 degrees C and 1 MPa oxygen. Benzyl alcohol can also be quantitatively converted to benzoic acid at 60 degrees C even under an atmospheric pressure, showing great advantages in green chemistry. The catalysts are stable, poison resistant, and reusable with little activity loss due to metal leaching. The silane coupling agent played several functions in this approach: (1) coordinating with gold species by the thiol group to benefit formation of monodispersed Au nanopartides; (2) reacting with phenolic resins by silanol groups to form relatively "rigid" composite framework; (3) pore-forming agent to generate secondary pores in carbon pore walls, which lead to higher surface area, larger pore volumes, and higher accessibility to to the gold nanopartides. Complete removal of the silica component proves to have little effect on the catalytic performance of entrapped Au nanoparticles.

Preparation of Gold Nanoparticles Loaded Hollow Silica Spheres and Their Catalytic Performance

In Situ Growth of Gold Nanoparticles on SiO2/lanthanide–polyoxometalates Composite Spheres: an Efficient Catalytic and Luminescent System

Facile And Controllable Fabrication Of Gold Nanoparticles-Immobilized Hollow Silica Particles And Their High Catalytic Activity

Bifunctional Composite Microspheres of Silica/lanthanide-Polyoxometalates/au: Study on Luminescence and Catalytic Properties

Preparation of Highly Active Silica-Supported Au Catalysts for Co Oxidation by A Solution-Based Technique

Synthesis of Stable Au–SiO2 Composite Nanospheres with Good Catalytic Activity and SERS Effect

Synthesis of tetra-layer polymer composite microspheres and the corresponding hollow polymer microspheres with Au nanoparticles functionalized movable cores

Hollow mesoporous organosilica nanospheres with multiple tiny silver nanoparticles: A polymer mediated growth approach and catalytic application

Facile in Situ Preparation of Noble Metal Nanoparticles Supported on Silica

A General and Feasible Method for the Fabrication of Functional Nanoparticles in Mesoporous Silica Hollow Composite Spheres

Bifunctional Polymer Brush Reactor for in Situ Synthesis of Hollow Silica-Supported Gold Nanocatalysts.

Preparation of polymer microspheres with reactive epoxy group and amino groups as stabilizers for gold nanocolloids with recoverable catalysis

Preparation Of Hollow Submicrospheres With Ordered Porous Sio2 Shell And Multiple Aupt Nanoalloy Cores And Their High Catalytic Activity

Aggregation-Free Gold Nanoparticles In Ordered Mesoporous Carbons: Toward Highly Active And Stable Heterogeneous Catalysts

Preparation and Characterization of Ag Nanoparticles Embedded in Hierarchically Porous Monolithic Silica

Nanoscale gold intercalated into mesoporous silica as a highly active and robust catalyst.

Synthesis of Gold Nanoparticles on Rice Husk Silica for Catalysis Applications

Gold Nanoparticles Supported on Mesoporous Silica and Their Catalytic Application

Facile Fabrication Method And Characterization Of Hollow Ag/Sio2 Double-Shelled Spheres

Controllable Preparation of Monodisperse Mesoporous Silica from Microspheres to Microcapsules and Catalytic Loading of Au Nanoparticles

A Simple Method of Preparing Ag Nanoparticles Coated Silica Colloidal Crystals and Polymer-Ag Nanoparticles Composite Macroporous Films