Abstract:Along with the widespread applications of various energy storage and conversion devices, the prices of precious metal platinum (Pt) and transition-metal cobalt/nickel keep continuously growing. In the future, designing high-efficiency nonprecious-metal catalysts based on low-cost iron (Fe) and manganese (Mn) metals for hydrogen evolution reaction (HER) and oxygen reduction reaction (ORR) is fairly critical for commercial applications of hydrogen fuel cells. In this study, for the first time, we design novel three-dimensional (3D) hybrid networks consisting of manganese oxide (MnO)-modified, iron carbide (Fe3C)-embedded, and boron (B)/nitrogen (N) codoped hierarchically porous carbon nanofibers (denoted ). After optimizing the pyrolysis temperatures, the optimal catalyst displays the best HER and ORR catalytic activities in an alkaline solution. As expected, the HER onset potential (Eonset) and the potential at a current density of −10 mA cm–2 for in 1.0 M KOH are just 36 and 194 mV more negative than the state-of-the-art 20 wt % Pt/C catalyst with more superior stability. In particular, the catalyst shows excellent ORR catalytic activity with a more positive Eonset (0.946 V vs RHE), a more positive half-wave potential (E1/2 = 0.868 V vs RHE), better long-term stability, and higher methanol tolerance surpassing the commercial 20 wt % Pt/C (Eonset = 0.943 V vs RHE, E1/2 = 0.854 V vs RHE) and most previously reported precious-metal-free catalysts in 0.1 M KOH. The synergistic effects of 3D hierarchically macro-/mesoporous architectures, advanced charge transport capacity, abundant carbon defects/edges, abundant B (2.3 atom %) and N (4.9 atom %) dopants, uniformly dispersed Fe3 NPs, and MnO nanocrystallines are responsible for the excellent HER/ORR catalytic activities of the catalyst.The Supporting Information is available free of charge at https://pubs.acs.org/doi/10.1021/acsami.1c23731.Detailed conditions for electrospinning; physical characterization of precursor networks and T networks; Electrochemical characterization of various T networks toward HER and ORR in the alkaline condition; DSC-TGA of the precursor; SEM images of and ; nitrogen adsorption–desorption isotherm, Raman spectrum, and XRD pattern of ; TEM images and SEM-EDX mapping of ; high-resolution O 1s spectra and pore size distribution plots of different T samples; TCV curves recorded at different potential scanning rates from 30 to 110 mV s–1 for T networks; equivalent electrical circuit utilized for fitting electrochemical impedance spectra; and HER/ORR LSV curves of different control samples (PDF)This article has not yet been cited by other publications.

Highly Active Carbon/alpha-MnO2 Hybrid Oxygen Reduction Reaction Electrocatalysts

Highly Active Carbon/α‐MnO2 Hybrid Oxygen Reduction Reaction Electrocatalysts

Facile Construction Of Manganese Oxide Doped Carbon Nanotube Catalysts With High Activity For Oxygen Reduction Reaction And Investigations Into The Origin Of Their Activity Enhancement

Oxygen Reduction Electrocatalyst Based on Strongly Coupled Cobalt Oxide Nanocrystals and Carbon Nanotubes.

Hybrid shells of MnO2 nanosheets encapsulated by N-doped carbon towards nonprecious oxygen reduction reaction catalysts

Self-deposition of Pt nanocrystals on Mn3O4 coated carbon nanotubes for enhanced oxygen reduction electrocatalysis

Design and Synthesis of Conductive Carbon Polyhedrons Enriched with Mn-Oxide Active-Centres for Oxygen Reduction Reaction

Manganese Oxide-Induced Strategy to High-Performance Iron/nitrogen/carbon Electrocatalysts with Highly Exposed Active Sites.

Efficient Oxygen Reduction Electrocatalysis on Mn3O4 Nanoparticles Decorated N-doped Carbon with Hierarchical Porosity and Abundant Active Sites

Bimetallic Mn and Co Encased Within Bamboo-Like N-doped Carbon Nanotubes As Efficient Oxygen Reduction Reaction Electrocatalysts.

Dual-MOFs-Derived Fe and Mn Species Anchored on Bamboo-like Carbon Nanotubes for Efficient Oxygen Reduction as Electrocatalysts

Restructured Fe−Mn Alloys Encapsulated by N‐doped Carbon Nanotube Catalysts Derived from Bimetallic MOF for Enhanced Oxygen Reduction Reaction

Manganous oxide nanoparticles encapsulated in few-layer carbon as an efficient electrocatalyst for oxygen reduction in alkaline media

Enabling highly efficient electrocatalytic oxygen reduction and evolution reaction by established strong MnO/Co-support interaction

Carbon-Free, Binder-Free MnO2@Mn Catalyst for Oxygen Reduction Reaction.

Graphitic Carbon Nitride (g-C3N4) Derived Bamboo-like Carbon Nanotubes/Co Nanoparticles Hybrids for Highly Efficient Electrocatalytic Oxygen Reduction.

Highly Active and Extremely Stable L10-PtCoMn Ternary Intermetallic Nanocatalyst for Oxygen Reduction Reaction

Strongly Coupled MnO 2 Nanosheets/Silver Nanoparticles Hierarchical Spheres for Efficient Oxygen Reduction Reaction Electrocatalysis

Facile Synthesis of Manganese‐Oxide‐Containing Mesoporous Nitrogen‐Doped Carbon for Efficient Oxygen Reduction

Manganese Oxide/Iron Carbide Encapsulated in Nitrogen and Boron Codoped Carbon Nanowire Networks as Accelerated Alkaline Hydrogen Evolution and Oxygen Reduction Bifunctional Electrocatalysts

A Facile and Low-Cost Synthesis of MnOx/Mn2N-N-C Nanohybrid As an Advanced Oxygen Reduction Electrocatalyst