Abstract:Graphene, a single-atom-thick sheet of hexagonally arrayed sp2-bonded carbon atoms, has got a significant attention due to its unique electronic [1], mechanical [2], and thermal [3] properties all derived from the unique details of its electronic band structure. Due to its flexibility, graphene provides infinite possibilities in various fields [4, 5] and the peculiar dispersion relation of carbon’s π electrons is responsible for its unique properties [1]. There are different ways to produce “pristine” graphene. The graphene synthesis can be mainly classified into exfoliation [6], chemical vapor deposition (CVD) [7], arc discharge [8], and reduction of graphene oxide (GO) [9]. One method for isolation of a sheet of graphene is through the mechanical exfoliation from a graphite crystal, but this is not scalable beyond one small flake of graphene, making graphenewith lateral dimensions on the order of tens to hundreds ofmicrometers. But reports are also showing the development of patterned graphene through the mechanical exfoliation of patterned graphite. The important large-scale synthesis of graphene includes the thermal decomposition of silicon carbide [10] andCVDgrowth.The formation of carbon layers with sp2 bonding, on the SiC substrate could be obtained through the sublimation of Si by heating theC-face or Si-face in ultrahigh vacuum (UHV) at temperatures ranging from 1000 to 1500 ∘C and the thermal decomposition of hydrocarbons. CVD method has raised much attention for graphene synthesis due to high quality with large surface area. Gas-phase synthesis of graphene platelets and arc discharge synthesis of multilayered graphene are also reported. Exfoliation of graphite in solvents is a method for obtaining dispersions of GO to yield individual layers of GO and offers potential for the production of costeffective, large-scale production of graphene [9]. Based on recent studies, GO consists of phenol hydroxyl and epoxide functional groups on the top and bottom surfaces of each sheet and sp2-hybridized carbons containing carboxyl and carbonyl groups mostly at the sheet edges and these groups offer tremendous opportunities for access to functionalized graphene-based materials [11].The oxidation

Controlled Synthesis of Few-Layered Graphene Sheets on a Large Scale Using Chemical Exfoliation

Size-controlled Synthesis of Graphene Oxide Sheets on a Large Scale Using Chemical Exfoliation

Synthesis Of Graphene Nanosheets Via Oxalic Acid-Induced Chemical Reduction Of Exfoliated Graphite Oxide

Covalent Synthesis of Organophilic Chemically Functionalized Graphene Sheets

Facile and Size-Controllable Preparation of Graphene Oxide Nanosheets Using High Shear Method and Ultrasonic Method

Synthesis of graphene oxide sheets with controlled sizes from sieved graphite flakes

Efficient Preparation Of Large-Area Graphene Oxide Sheets For Transparent Conductive Films

Enhanced Exfoliation Efficiency of Graphite into Few-Layer Graphene Via Reduction of Graphite Edge

Facile Synthesis of Graphene Nanosheets Via Fe Reduction of Exfoliated Graphite Oxide.

Electrolyte engineering for the mass exfoliation of graphene oxide across wide oxidation degrees

From Graphite to Graphene: Direct Liquid-Phase Exfoliation of Graphite to Produce Single- and Few-Layered Pristine Graphene

Ultrasonication-Assisted Controllable Self-Assembly of Graphene Oxide

Synthesis of High-Quality Graphene with a Pre-Determined Number of Layers

Controlling oxidation degree and crystallinity to achieve high Young's modulus of graphene derivatives

Solvothermal Reduction of Chemically Exfoliated Graphene Sheets

Graphene preparation and graphite exfoliation

Facile Synthesis and Characterization of Graphene Nanosheets

Fundamental of Graphene

New Insight of High Temperature Oxidation on Self-Exfoliation Capability of Graphene Oxide

Advancement In Liquid Exfoliation Of Graphite Through Simultaneously Oxidizing And Ultrasonicating

Water-Enhanced Oxidation Of Graphite To Graphene Oxide With Controlled Species Of Oxygenated Groups