Abstract:A modified nano-calcium carbonate (R-CCR) was prepared by coating a layer of unsaturated hydroxylfatty acid on the surface of CCR powders using a solid state method; the latter were commercial nano-CaCO 3 modified with stearic acid. FTIR studies indicate that the modifier is combined on the surface of CaCO 3 . PP/EPDM/nano-CaCO 3 ternary composites were prepared by a melt-mixing method. SEM and TEM were utilized to examine the morphology of the composites. The tensile fractured surface of PP/EPDM/R-CCR showed a fibroid morphology and large-scale yield deformation. The impact fractured surface showed that the amount of cavities in the PP/EPDM/R-CCR system was increased, however their size diminished obviously. R-CCR particles were dispersed uniformly in the PP matrix, and their compatibility was distinctly improved as compared to CCR when the amount of R-CCR was 15 h −1 . The tensile strength remained nearly constant (reduced from 27.6 MPa to 27.5 MPa), while the impact strength increased from 9.6 kJ/m 2 to 15.4 kJ/m 2 as CCR was replaced by R-CCR. Meanwhile, the bending strength and bending modulus also increased correspondingly. Furthermore, the impact strength of PP/EPDM/R-CCR was maintained at a high level (15.4 kJ/m 2 ), which was more than the sum of that of PP/EPDM and PP/R-CCR (6.6 kJ/m 2 and 6.1 kJ/m 2 respectively). This indicates that the R-CCR and EPDM have a significant synergistic toughening effect on PP while maintaining the strength and modulus of virgin PP. Both the storage modulus G′ and loss modulus G″ of PP/EPDM and PP/EPDM/R-CCR composites increase with increasing frequency, but the values of G′ and G″ of the tertiary composite are relatively higher than those of the binary system. The loss factor and viscosity decrease with increasing frequency, but there is little difference between tertiary and binary composites. The apparent viscosity η of the tertiary system containing R-CCR is lower than that of the tertiary system containing CCR and virgin PP. The viscosity of the composites sig-nificantly decreases with increasing shear rate. The mea-sured mechanical properties of the composites indicate that replacing CCR with R-CCR for binary composites could simultaneously enhance the toughness and strength of PP.

Rheological Properties of PP/CaCO3 Micron-Nano Composite Blends Processing Based on Elongation Rheology Via Vane Extruder

Effective Enhancement of a Carbon Nanothread on the Mechanical Properties of the Polyethylene Nanocomposite

The polymer melt swelling behavior in micro-extrusion process for preparation of continuous carbon fiber reinforced PP prepreg filament

Preparation of high melt strength polypropylene by the reactive extrusion process and its foaming application

Influence of Reduced Graphene Oxide on the Rheological Response and Chain Orientation on Shear Deformation of High Density Polyethylene

Morphology, rheology, and mechanical properties of polylactide/ poly(ethylene-co-octene) blends

Rheological Properties and Morphological Evolutions of Polypropylene/Ethylene-Butene Copolymer Blends

Effect of Unsaturated Hydroxyl-Fatty Acid Modified Nano-Caco3 on the Morphological and Rheological Behavior of PP

Melt extrudate swell behavior of multi‐walled carbon nanotubes filled‐polypropylene composites

STUDIES ON INFLUENCES OF VISCOELASTIC PROPERTIES ON MELT EXTRUSION OF CARBON NANOTUBES-FILLED ISOTACTIC POLYPROPYLENE COMPOSITES

Study on the Properties and Structure of Polypropylene Modified with Nano-Sized CaCO_3

Elongational Flow Field Processed Ultrahigh Molecular Weight Polyethylene/Polypropylene Blends with Distinct Interlayer Phase for Enhanced Tribological Properties

Rheological Properties of Neat and Calcium Carbonate Particles Filled Polypropylene Blends under Axial Vibration Force Field

Improving Mechanical Performance of Immiscible Polypropylene/poly(methyl Methacrylate) Blends by Adding Calcium Carbonate Nanoparticles with Bifunctions of Compatibilization and Β-Nucleation

The effect of elastomeric nano-particles on the mechanical properties and crystallization behavior of polypropylene

A novel PLA/P(3HB-co-4HB)/MWCNT composite featuring enhanced mechanical properties and excellent thermal stability based on elongational rheology

Effect of Morphology Development on the Low‐temperature Tensile Properties of PP / POE Blends

Morphology, thermal behavior, rheological, and mechanical properties of polypropylene/polystyrene blends based on elongation flow

Rheological Behavior and Nonisothermal Crystallization of Polypropylene/Epoxidized Natural Rubber Blends

Study of Property of Nano-ZnO/PP and ZnO/CaCO3/PP Composites

Poly(lactic acid)/poly(ε-caprolactone) blends: Separate effects of nanocalcium carbonate and glycidyl methacrylate on interfacial characteristics