Hot Pressing Titanium Metal Matrix Composites Reinforced with Graphene Nanoplatelets Through an In-Situ Reactive Method

X. N. Mu,H. M. Zhang,H. N. Cai,Q. B. Fan,Y. Wu,Z. J. Fu,Q. X. Wang

DOI: https://doi.org/10.1063/1.4983594

2017-01-01

AIP Conference Proceedings

Abstract:This study proposed an in-situ reactive method that uses graphene as a reinforcement to fabricate titanium metal matrix composites (TiMMCs) through powder metallurgy processing route. The volume fraction of graphene nanoplatelets was 1.8% vol, and the pure titanium was used as a matrix. The Archimedes density, hardness, microstructure and mechanical properties of specimens were compared under different ball milling times (20 min and 2.5 h) and hot pressing temperatures (900 degrees C, 1150 degrees C, and 1300 degrees C,). The ultimate tensile strength of 630 MPa, which demonstrated a 27.3% increase compared with pure Ti, was achieved under a ball milling time of 20 min. Elongation increased with increasing temperature. When the ball milling time and hot pressing temperature were increased to 2.5 h and 1300 degrees C, respectively, the ultimate tensile strength of the composites reached 750 MPa, showing an increase of 51.5% compared with pure Ti.