Bi2O3-doping Controlled Magnetic and Dielectric Properties of Low-Temperature Co-Fired NiCuZn Ferrite for High-Frequency Applications
Li Guo,Jie Li,Yan Yang,Gang Wang,Yiheng Rao,Gongwen Gan,Huaiwu Zhang
DOI: https://doi.org/10.1007/s10854-019-01919-4
2019-01-01
Journal of Materials Science Materials in Electronics
Abstract:NiCuZn ferrite, due to its good magnetic properties, is a near optimal material for low-temperature co-fired ceramic (LTCC) filter applications. In this study, low temperature (860 °C and 880 °C) co-fired Ni0.26Cu0.22Zn0.52Fe2O4 ferrites with different quantities of Bi2O3 (1–11 wt% with an increment of 2 wt%) were synthesized using a solid-state reaction. The effect of the Bi2O3 additive on phase formation, microstructure, magnetic permeability, and dielectric permittivity are investigated. The results indicate that a suitable amount of Bi2O3 doping can increase both bulk density and the magnetic properties. The superfluous Bi2O3 and Fe3+ ions form Bi25FeO39, which improves the dielectric properties. More specifically, the sample with 5 wt% Bi2O3, sintered at 880 °C, shows excellent magnetic permeability (μ′ ~ 130 @ 1–10 MHz), low magnetic loss (tanδμ ~ 0.026), and a high cut-off frequency (~ 100 MHz). The sample with 9 wt% Bi2O3, sintered at 880 °C, exhibits excellent dielectric permittivity (ε′ ~ 14.5 @ 1–400 MHz), low dielectric loss (tanδε ~ 0.0075), and a high cut-off frequency (~ 1 GHz). These observations indicate that NiCuZn ferrites, with the right amount of Bi2O3, are promising candidate materials for LTCC applications.