Abstract:Cr2O3-TiO2 (CrTiO) composite powders were synthesized via high temperature solid-state reaction method. CrTiO coating with different Cr2O3 content were prepared from plasma spraying using CrTiO composite powders as spraying feed respectively. X ray diffraction analysis (XRD) and scanning electron microscopy (SEM) analysis were taken to characterize the phase components and microstructure, respectively. Electromagnetic parameters (including complex permittivity and complex permeability) of CrTiO coating were characterized and studied through a network vector analyzer. Electromagnetic-wave absorption property of CrTiO coating with different coating thickness were also examined. Results of XRD show that the main composition of the CrTiO composites are TiO2 and Cr0.12Ti0.78O1.34. Complex permittivity and complex permeability of coating increase with the increase of Cr2O3 content, which is ascribed that the enhancement of carrier concentration, relaxation polarization, electron polarization and magnetic polarization etc. Reflectivity results show that the composite coating displays electromagnetic attenuation at 8.2 GHz-12.4 GHz (generally called the X-band) for 15% Cr2O3 content coating with a sample thickness 1.9 mm. The peak value of the reflection loss reaches -10dB can be achieved at 8.2 GHz-10.2 GHz. Moreover, a frequency selective surface (FSS) coupled by a circular element and four square elements is used to further enhanced the microwave absorption performance of coating. The results show that the microwave absorption performance of the absorbing coating mainly depend on the frequency selective surface, Cr2O3 content and thickness of the CrTiO coating. These results imply that CrTiO coating have a potential as microwave absorbing materials for electromagnetism applications. (C) 2019 Elsevier B.V. All rights reserved.

Electromagnetic-wave Absorption Property of Cr2O3–TiO2 Coating with Frequency Selective Surface