Abstract:The catalytic conversion of dinitrogen (N-2) into ammonia under ambient conditions represents one of the Holy Grails in sustainable chemistry. As a potential alternative to the Haber-Bosch process, the electrochemical reduction of N-2 to NH3 is attractive owing to its renewability and flexibility, as well as its sustainability for producing and storing value-added chemicals from the abundant feedstock of water and nitrogen on earth. However, owing to the kinetically complex and energetically challenging N-2 reduction reaction (NRR) process, NRR electrocatalysts with high catalytic activity and high selectivity are rare. In this contribution, as a proof-of-concept, we demonstrate that both the NH3 yield and faradaic efficiency (FE) under ambient conditions can be improved by modification of the hematite nanostructure surface. Introducing more oxygen vacancies to the hematite surface renders an improved performance in NRR, which leads to an average NH3 production rate of 0.46 mu g h(-1) cm(-2) and an NH3 FE of 6.04 % at -0.9 V vs. Ag/AgCl in 0.10 m KOH electrolyte. The durability of the electrochemical system was also investigated. A surprisingly high average NH3 production rate of 1.45 mu g h(-1) cm(-2) and a NH3 FE of 8.28 % were achieved after the first 1 h chronoamperometry test. This is among the highest FEs reported so far for non-precious-metal catalysts that use a polymer-electrolyte-membrane cell and is much higher than the FE of precious-metal catalysts (e.g., Ru/C) under comparable reaction conditions. However, the NH3 yield and the FE dropped to 0.29 mu g h(-1) cm(-2) and 2.74 %, respectively, after 16 h of chronoamperometry tests, which indicates poor durability of the system. Our results demonstrate the important role that the surface states of transition-metal oxides have in promoting electrocatalytic NRR under ambient conditions. This work may spur interest towards the rational design of electrocatalysts as well as electrochemical systems for NRR, with emphasis on the issue of stability.

Promoting Electrocatalytic Nitrogen Reduction to Ammonia Via Fe-boosted Nitrogen Activation on MnO2 Surfaces

Mesoporous MnO2 nanosheets for efficient electrocatalytic nitrogen reduction via high spin polarization induced by oxygen vacancy

Fe2Mo3O8/XC-72 electrocatalyst for enhanced electrocatalytic nitrogen reduction reaction under ambient conditions

Highly Selective Electrochemical Reduction Of Dinitrogen To Ammonia At Ambient Temperature And Pressure Over Iron Oxide Catalysts

Oxygen-Coordinated Single Mn Sites for Efficient Electrocatalytic Nitrate Reduction to Ammonia

Nitrogen-coordinated Single Fe Sites for Efficient Electrocatalytic N2 Fixation in Neutral Media

Modulating Oxygen Vacancies of TiO2 Nanospheres by Mn-Doping to Boost Electrocatalytic N2 Reduction

Introducing oxygen vacancies in a bi-metal oxide nanosphere for promoting electrocatalytic nitrogen reduction

Modulating Nitrogen Adsorption Mode and Microenvironment of Active Sites for Boosting Electrochemical Nitrogen Reduction

Boosting Electrocatalytic N2 Reduction to NH3 on Β-Feooh by Fluorine Doping

FeNi bimetallic oxides derived from MOFs as precursors promote efficient electrochemical synthesis of ammonia

FeMo-N nanosheet arrays supported on nickel foam for efficient electrocatalytic reduction of N2 to NH3 at ambient condition

Regulating the Electronic Configuration of Supported Iron Nanoparticles for Electrochemical Catalytic Nitrogen Fixation

Repairable body-centered cubic Fe 0 anchoring on porous hollow nitrogen-doped carbon spheres with adjusting electron distribution for efficient electrocatalytic ammonia synthesis

Highly selective environmental electrocatalytic nitrogen reduction to ammonia on Fe2(MoO4)3/C composite electrocatalyst

Periodic Adjacent Pd‐Fe Pair Sites for Enhanced Nitrate Electroreduction to Ammonia via Accelerating Proton Relay

Electrocatalytically Active Fe‐(O‐C2)4 Single‐Atom Sites for Efficient Reduction of Nitrogen to Ammonia

Electroreduction of Nitrate to Ammonia on Atomically-Dispersed Cu-N4 Active Sites with High Efficiency and Stability

Enhanced Electrocatalytic Nitrate-to-Ammonia Performance from Mott-Schottky Design to Induce Electron Redistribution

Electrocatalytic Hydrogenation of N2 to NH3 by MnO: Experimental and Theoretical Investigations.

Boosting Electrochemical Nitrate Reduction to Ammonia by Fe Doped CuO/Co3O4 Nanosheet/Nanowire Heterostructures