Abstract:Dielectric ceramics with low permittivity (epsilon(r)), high quality factor (Qxf), and near-zero resonant frequency (tau(f)) in the microwave bands are key materials used in fifth/sixth-generation (5G/6G) telecommunication, while tau(f) of most low-epsilon(r) microwave dielectric ceramics is relatively negative. In this work, the first low-epsilon(r) Ga-based ceramic SrGa12O19 with an anomalous positive tau(f) was reported, and the causes of the positive tau(f), intrinsic polarization, and loss mechanism were systematically studied. X-ray diffraction (XRD) and transmission electron microscopy (TEM) revealed that the SrGa12O19 ceramic formed a pure hexagonal magnetoplumbite structure with spinel blocks and rock-salt blocks stacked along the crystallographic c-axis. When sintered at 1430 degrees C, it possessed the optimal microwave dielectric properties of a low epsilon(r) of 14.46, high Qxf of 64,705 GHz, and exceptional positive tau(f) of +55.7 ppm/degrees C, along with a low linear thermal expansion coefficient (alpha(L)) of 11.617 ppm/degrees C. The large positive deviation between epsilon(r) and epsilon(r(C-M)) of 45.31% resulted from the rattling effect of atoms in the rock-salt block. The unique positive tau(f) (+55.7 ppm/degrees C) was governed by the rattling effect, resulting in a positive tau(alpha m) (the temperature coefficient of ion polarizability) of 8.489 ppm/degrees C and a large negative temperature coefficient of permittivity (tau(epsilon)) of -132.864 ppm/degrees C. Phillips-Vechten-Levine (P-V-L) chemical bond theory revealed greater contributions of the spinel block to bond ionicity (f(i), 52.95%), permittivity (epsilon, 55.15%), bond energy (E, 56.87%), and lattice energy (U, 74.88%) than those of the rock-salt block. The intrinsic dielectric properties were analyzed using infrared (IR) reflectivity spectra. The favorable performance of the SrGa12O19 ceramic indicated that it is a novel tau(f) compensator. This selection of compounds with different structural layer combinations provides a new idea for exploring excellent microwave dielectric ceramics.

Novel low-permittivity microwave dielectric ceramics in garnet-type Ca4ZrGe3O12

Crystal Structure, Infrared Reflectivity Spectra and Microwave Dielectric Properties of CaAl2O4 Ceramics with Low Permittivity

Crystal Structure, Vibrational Spectroscopy, and Microwave Dielectric Properties of CaAl4O7 Ceramics with Low Permittivity

Structure, Raman spectra and microwave dielectric properties of novel garnet-type Ca<sub>3</sub>MZrGe<sub>3</sub>O<sub>12</sub> (M = Co, Zn) ceramics

SrGa12O19: the First Low-Εr Ga-based Microwave Dielectric Ceramic with Anomalous Positive Τf

The Apparent Difference in Microwave Dielectric Properties of Ca3MZnGe3O12 (M = Zr, Sn) Garnets Originating from Compression and Rattling Effects

Correlation between crystal structure and microwave dielectric properties of two garnet-type ceramics in rare-earth-free gallates

Tuning of microwave dielectric properties of garnets Ca3Mg2CV2O12 (C = Si, Ti) through compression and expansion effects

A novel low loss rare-earth germanate La4GeO8 microwave dielectric ceramic with orthorhombic structure

Influence of B-site rare-earth Yb cation on the crystal structure and microwave dielectric properties of Ca3Yb2Ge3O12 garnet ceramics

Relationship between the structure and microwave dielectric properties of garnet ceramics Ca3B2GeV2O12 (B = Mg, Mn)

Rattling effects on microwave dielectric properties of Ca3TiBGe3O12 (B = Mg, Zn) garnets

Li2AGeO4 (A = Zn, Mg): Two novel low-permittivity microwave dielectric ceramics with olivine structure

Low-Temperature Firing and Microwave Dielectric Properties of Ca[(Li13Nb23)0.8Ti0.2]O3Ceramics with ZnB2O4Glass Addition

LiCa3ZnV3O12: A Novel Low-Firing, High Q Microwave Dielectric Ceramic

A Novel Low-Firing Microwave Dielectric Ceramic Li 2 ZnGe 3 O 8 with Cubic Spinel Structure

Structure, Microwave Dielectric Properties, and Infrared Reflectivity Spectrum of Olivine Type Ca2GeO4 Ceramic

A novel low-permittivity Lu2MgAl4SiO12 microwave dielectric ceramic with garnet-type structure

Structure, Raman spectra and properties of two low-ε microwave dielectric ceramics Ca3B2Ge3O12 (B = Al, Ga)

Vibrational studies and microwave dielectric properties of Ca3Te2Zn3O12 ceramic with garnet structure

Chemical bond characteristics, Raman spectra, and microwave dielectric properties of garnet ceramics Ca3B2ZnGa2O12 (B = Nb, Sb)