Study of Building an Integrated Annulus Fibrosus-Nucleus Pulposus Biphasic Scaffold Based on Bone Matrix Gelatin and Cartilage Matrix

伍耀宏,徐宝山,杨强,马信龙,夏群,李秀兰,胡永成,张杨,张春秋

DOI: https://doi.org/10.3760/cma.j.issn.0253-2352.2013.02.014

2013-01-01

Abstract:Objective To fabricate an integrated annulus fibrosus-nucleus pulposus biphasic scaffolds based on bone matrix gelatin and acellular cartilage matrix,and to detect its property and cell compatibility.Methods An integrated annulus fibrosus-nucleus pulposus biphasic scaffold was fabricated by the following steps: preparing the hollow bone matrix gelatin ring,injecting the acellular cartilage homogenate into the center of the bone matrix gelatin ring,and freeze drying.Sample slices were stained with Hoechst 33258,picrosirius and HE.The internal structure of the scaffold was observed under a scanning electron microscope.The porosity and water absorption of the scaffold were also evaluated.Compressive mechanical property under wet situation was tested.The annulus fibrosus and nucleus pulposus cells were isolated from sheep disc and separately implanted into the corresponding sites of the scaffold,and biocompatibility of the scaffold was evaluated by scanning electron microscope and live/dead cell staining.Results Hoechst 33258 staining showed no residual cells,picrosirius staining was positive,and HE staining showed two parts linked closely.Under scanning electron microscope,the scaffold had porous structure,and the average pore size was 401.4±13.1 μm for annulus fibrosus,and 112.4±21.8 μm for nucleus pulposus.The porosity and water absorption of the scaffold was 73.37％±2.56％ and 655.7％±78.6％,respectively.The average compressive elastic modulus of the scaffold (49.06 ±15.57) kpa was smaller than that of the native disc (135.9±28.9) kPa.Scanning electron microscope showed cells adhered on the scaffold surface,with secreted matrix around them,and live/dead cells staining showed cells with good activity on scaffolds.Conclusion The integrated annulus fibrosus-nucleus pulposus scaffold based on bone matrix gelatin and cartilage matrix is an ideal artificial disc material,in view of well pore size,closely linked boundary,and good biocompatibility.