Abstract:BACKGROUND: The expanded polytetrafluoroethylene (ePTFE) vascular grafts hold promise for enhanced healing, extended suture retention, kink reduction and compression resistance. But thrombus formation still limits its use for revascularization of small-caliber vessels. It is the surface of ePTFE vascular graft that contacts with the blood. The current study focused on surface modification of ePTFE materials to improve its blood compatibility. OBJECTIVE: To characterize the heparin/alginate (H/A) gel modified ePTFE vascular graft and investigate the hemocompatibility and histocompatibility of the graft. DESIGN: Observation experiment. SETTING: Laboratory for Nanomedicine and Biosensor, Biomedicine Engineering Center, Harbin Institute of Technology. MATERIALS: The GORE-TEX ePTFE vascular grafts were 4 mm in internal diameter. Sodium alginate and 1-ethyl-3- (3-dimethylaminopropyl)-carbodiimide hydrochloride (EDC) were purchased from Sigma. Heparin sodium salt was obtained from Calbiochem. Nafion and chitosan were purchased from Aldrich company. Human α-thrombin and AT III were purchased from Haematologic Technologies, Inc. S-2238 was purchased from Chromogenix. METHODS: This study was performed at the Laboratory for Nanomedicine and Biosensor, Biomedicine Engineering Center, Harbin Institute of Technology between May 2006 and June 2007. The graft was first modified with Nafion and then Chitosan/Nafion/Chitosan multilayer. Following the impregnation of heparin and alginate, covalent crosslinking was performed using ethylenediamine and EDC. Some characterization methods were employed: stastic water contact angle for the hydrophilicity; SEM for the surface morphology; ATR-FTIR for the surface chemical characteristics; APTT and PT, percent hemolysis and Chromogenic assay for the hemocompatibility of the ePTFE vascular graft after modification. MAIN OUTCOME MEASURES: ①Static water contact angles. ②Characterization of the surface morphology and platelet adhesion by SEM. ③ATR-FTIR ④APTT and PT. ⑤Percent hemolysis ⑥Chromogenic assay for heparin activity. RESULTS: ①ATR-FTIR revealed the presence of -CO-NH- at 1626 cm-1. ②The water contact angle was greatly decreased from (125±1)° to (84±2)°. ③The prolonged APTT and PT, low percent hemolysis(0.065%) and low amount of platelet adhesion assay showed the H/A gel impregnated graft had good blood compatibility. ④Chromogenic assay showed the modified graft was less thrombogenic than the bare one, and the H/A coating had good stability in. PBS buffer. CONCLUSION: The H/A modified ePTFE vascular graft has great potential in applications utilizing small-diameter vascular grafts.

Hemocompatibility Evaluation of Small-Caliber Expanded Polytetrafluoroethylene Vessel with Heparin Collagen Layer-by-layer Assembly Multilayer

Local Hemodynamic Disturbance Accelerates Early Thrombosis Of Small-Caliber Expanded Polytetrafluoroethylene Grafts

Improving the hemocompatibility of a porohyperelastic layered vascular graft using luminal reversal microflows

Small-caliber expanded poly(tetrafluoroethylene) vascular prosthesis impregnated with heparin and polyvinyl alcohol gel

Heparin/Collagen-REDV Modification of Expanded Polytetrafluoroethylene Improves Regional Anti-thrombosis and Reduces Foreign Body Reactions in Local Tissues

The Effect Of Heparin-Vegf Multilayer On The Biocompatibility Of Decellularized Aortic Valve With Platelet And Endothelial Progenitor Cells

Thromboresistant surface modification of expanded polytetrafluoroethylene vascular graft by impregnating covalently crosslinked gel of heparin and alginate

Application of Heparin/Collagen-REDV Selective Active Interface on Eptfe Films to Enhance Endothelialization and Anticoagulation

PLCL-TPU bi-layered artificial blood vessel with compliance matching to host vessel

Layer‐by‐layer Construction of Antibacterial and Anticoagulant Blood Contacting Materials

Natural anticoagulant and endothelial cell-compatible multilayer for endovascular stents surface modification

Biological Modifications of Eptfe for Promoting Endothelialization

Synthetic Eptfe Grafts Coated with an Anti-Cd133 Antibody-Functionalized Heparin/collagen Multilayer with Rapid in Vivo Endothelialization Properties.

PCL-based and Hirudin-containing Composite Nanofibers for Prolonged Anticoagulation Effect

Preparation and Biological Evaluations of Heparinized PLLA Films

The Novel Hybrid Polycarbonate Polyurethane / Polyester Three-Layered Large-Diameter Artificial Blood Vessel.

Construction and performance evaluation of Hep/silk-PLCL composite nanofiber small-caliber artificial blood vessel graft

Promotion of Endothelial Cell Adhesion and Antithrombogenicity of Polytetrafluoroethylene by Chemical Grafting of Chondroitin Sulfate

Bidirectional Elastic PTFE Small Diameter Artificial Blood Vessel Grafts and Surface Antithrombotic Functionalized Construction

Cytocompatibility and Blood Compatibility of Multifunctional Fibroin/Collagen/Heparin Scaffolds

Heparin/collagen multilayer as a thromboresistant and endothelial favorable coating for intravascular stent.