Abstract:Based on the disadvantages of the low thermal conductivity and easy leakage of the organic phase change energy storage material, Scaphium scaphigerum/graphene hybrid aerogel (SGA) with sparse porous structure was prepared by the template method and used as a thermally conductive reinforcing material to fabricate PEG forming composite PCMs of SGA/PEG. The results show that the three-dimensional pore structure of the SGA is composed of extremely thin graphene sheets interwoven and connected to each other. The EDA reducing agent can effectively remove the oxygen-containing functional groups, allowing the graphene sheets to re-adhere to the SC soft stencil and continuously aggregate, stack and self-assemble, resulting in thermally stable SGA. DSC result shows SGA/PEG composite has excellent overall thermal performance, especially SGA/PEG-8 with a latent thermal storage energy of 166.11 J/g, which is 99.35 % of that of pure PEG, and remains 99.20 % even after 100 heating-cooling cycles. The XRD, FT-IR and Raman spectroscopy results show that there is no chemical reaction in the SGA composite with PEG and that it is physically bonded. The TGA results show that the SGA can effectively conduct heat from the surface of the sample, showing a beneficial effect on the thermal stability of the composite. The SEM results directly demonstrate that the three-dimensional pore structure of the SGA is uniformly wrapped by PEG and that the surface of the lamellae is relatively smooth, without any significant accumulation of PEG. Furthermore, the shape-stable SGA/PEG exhibited a high thermal conductivity of 1.0621 W/(m K) which was enhanced to 378 % relative to pure PEG. This novel strategy offers enlightening prospects for the preparation of composite phase change materials with good thermal storage properties, thermal conductivity and thermal stability for a wide range of applications in energy storage.

Synthesis and characterization of polyethylene glycol/modified attapulgite form-stable composite phase change material for thermal energy storage

Preparation and Properties of Paraffin /LDPE /OMMT /graphite Phase Change Composite for Thermal Energy Storage

Polyethylene Glycol Confined in SiO2-Modified Expanded Graphite as Novel Form-Stable Phase Change Materials for Thermal Energy Storage

Polyethylene glycol/fumed silica composites as shape-stabilized phase change materials with effective thermal energy storage

Thermal energy storage performance of hierarchical porous kaolinite geopolymer based shape-stabilized composite phase change materials

Design of stearic acid/graphene oxide-attapulgite aerogel shape-stabilized phase change materials with excellent thermophysical properties

Dual-functional polyethylene glycol/graphene aerogel phase change composites with ultrahigh loading for thermal energy storage

Synthesis of the Polyethylene Glycol Solid-Solid Phase Change Materials with a Functionalized Graphene Oxide for Thermal Energy Storage

Thermal conductivity enhancement of polyethylene glycol/NF composite as stabilized phase change materials for thermal energy storage

Mica-stabilized polyethylene glycol composite phase change materials for thermal energy storage

Recent Progress in PEG-Based Composite Phase Change Materials

Efficient Enhancement of Heat Storage Capacity of Polyethylene Glycol Phase Change Material Based on a Novel Fly Ash Support

Preparation, Characterization and Thermal Properties of Fatty Acid Eutectics/bentonite/expanded Graphite Composites As Novel Form–stable Thermal Energy Storage Materials

Shape-stabilized composite phase change material PEG@TiO2 through in situ encapsulation of PEG into 3D nanoporous TiO2 for thermal energy storage

The Shape-Stabilized Phase Change Materials Composed Of Polyethylene Glycol And Various Mesoporous Matrices (Ac, Sba-15 And Mcm-41)

Experimental Investigation on the Characteristics of Polyethylene Glycol/Cement Composites As Thermal Energy Storage Materials

Scaphium scaphigerum/graphene hybrid aerogel for composite phase change material with high phase change enthalpy and high thermal conductivity for energy storage

Novel PEG/SiO2/SiO2–modified expanded graphite composite phase change materials for enhanced thermal energy storage performance

Graphene aerogel stabilized phase change material for thermal energy storage

Cost-Effective Biochar Produced from Agricultural Residues and Its Application for Preparation of High Performance Form-Stable Phase Change Material via Simple Method

Stable and reliable PEG/TiO2 phase change composite with enhanced thermal conductivity based on a facile sol-gel method without deionized water