Abstract:Fatigue failure is one of the most common failure modes for concrete structures. When subjected to fatigue loading, which may be induced either by vehicle load or by wind load, the damage of concrete would develop gradually due to the evolution of internal micro-cracks. Once the damage value exceeds a critical threshold, the concrete will lose its loading capacity. Therefore, knowledge about the fatigue damage evolution of concrete is crucial for evaluating its time-dependent deterioration as well as establishing the fatigue life prediction model of reinforced concrete structures. This paper dealt with an experimental research of stress level on fatigue performance of plain concrete based on the energy dissipation method. The developments of strain, stiffness degradation and energy dissipation were discussed in accordance with the obtained experimental data. Moreover, the parameter of effective area ratio, e.g. the ratio between the area of matrix and the area of concrete at the same cross section, was proposed to describe the fatigue damage as well as its evolution during the cyclic loading process. The results show that the developments of strain, stiffness degradation and fatigue damage can all be divided into three stages: (i) an instable and relatively brief stage due to the initiation of material original micro-cracks; (ii) a linear developing stage because of the propagation of internal micro-cracks; (iii) a rapid and unstable stage as a result of the growth and coalescence of cracks. In the linear developing stage, the value of strain rate remains constant approximately, irrespective of the stress level. In addition, the fatigue damage and stiffness degradation of concrete are closely linked to the stress level. With the increase of stress level, the fatigue damage enhances. But on the contrary, the stiffness degradation reduces when the stress level rises. The average value of single-cycle energy dissipation per unit volume in the second stage E-d,E-v increases exponentially due to the increasing of the stress level, and a fatigue life prediction model was developed by means of energy dissipation method. It is demonstrated that the fatigue life decreases with the absorbed energy of concrete and there is a linear relationship between the logarithmic fatigue life and E-d,E-v. (C) 2020 Elsevier Ltd. All rights reserved.

A Study on Fatigue Behaviors of Concrete under Uniaxial Compression: Testing, Analysis, and Simulation

Low-Cycle Fatigue Test of Circular Concrete Filled Tubular Columns

Experimental Study on the Fatigue Damage of High Strength Concrete under Uniaxial Compression

Detecting and Evaluation of Fatigue Damage in Concrete with Industrial Computed Tomography Technology

Research On Fatigue Strength Of Concrete Under Multi-Axial Compressive Cyclic Loading

Fatigue Performance of Prefabricated Composite T‐beams under Cyclic Overloading: an Experimental Study

Numerical Simulation of Fracture and Damage Behaviour of Concrete at Different Ages

Fatigue Behavior of Plain Concrete under Biaxial Compression: Experiments and Theoretical Model

Microscopic Multiple Fatigue Crack Simulation and Macroscopic Damage Evolution of Concrete Beam

Behavior of Concrete under Nonproportional Biaxial Fatigue Stresses with One Constant

Analytical Models of Concrete Fatigue: A State-of-the-Art Review

Experimental Prediction of Potential Fatigue Crack Path on Concrete Surface

Damage Theory Based Fatigue Simulation of Concrete Structure

Experiment-Based Fatigue Behaviors and Damage Detection Study of Headed Shear Studs in Steel–Concrete Composite Beams

Investigation of Stress Level on Fatigue Performance of Plain Concrete Based on Energy Dissipation Method

A Physically Motivated Model for Fatigue Damage of Concrete

Tension-softening Constitutive Relation and Numerical Simulation Method for Mode I Fatigue Crack Propagation in Concrete

Fatigue behavior of deep concrete beams with critical shear cracks

Experimental and Numerical Study on Mixed Mode I-II Fatigue Crack Propagation in Concrete

Physically Based Constitutive Modeling of Concrete Fatigue and Practical Numerical Method for Cyclic Loading Simulation

Analytical method for fatigue process of concrete structures