Synthesis and Physical Properties of Perovskite Sm1−x Sr X NiO3 (x = 0, 0.2) and Infinite-Layer Sm0.8Sr0.2NiO2 Nickelates

Chengping He,Xue Ming,Qing Li,Xiyu Zhu,Jin Si,Hai-Hu Wen

DOI: https://doi.org/10.1088/1361-648x/abfb90

2021-01-01

Journal of Physics Condensed Matter

Abstract:Recently, superconductivity at about 9-15K was discovered in Nd_1-xSr_xNiO_2 infinite-layer thin films, which has stimulated enormous interests in related rare-earth nickelates. Usually, the first step to synthesize this 112 phase is to fabricate the RNiO_3 phase, however, it was reported that the 113 phase is very difficult to be synthesized successfully due to the formation of unusual Ni^3+ oxidation state. And the difficulty of preparation is enhanced as the ionic radius of rare-earth element decreases. In this work, we report the synthesis and investigation on multiple physical properties of polycrystalline perovskites Sm_1-xSr_xNiO_3 (x = 0, 0.2) in which the ionic radius of Sm^3+ is smaller than that of Pr^3+ and Nd^3+ in related superconducting thin films. The structural and compositional analyses conducted by X-ray diffraction and energy dispersive X-ray spectrum reveal that the samples mainly contain the perovskite phase of Sm_1-xSr_xNiO_3 with small amount of NiO impurities. Magnetization and resistivity measurements indicate that the parent phase SmNiO_3 undergoes a paramagnetic-antiferromagnetic transition at about 224K on a global insulating background. In contrast, the Sr-doped sample Sm_0.8Sr_0.2NiO_3 shows a metallic behavior from 300K down to about 12K, while below 12K the resistivity exhibits a slight logarithmic increase. Meanwhile, from the magnetization curves, we can see that a possible spin-glass state occurs below 12K in Sm_0.8Sr_0.2NiO_3. Using a soft chemical reduction method, we also obtain the infinite-layer phase Sm_0.8Sr_0.2NiO_2 with square NiO_2 planes. The compound shows an insulating behavior which can be described by the three-dimensional variable-range-hopping model. And superconductivity is still absent in the polycrystalline Sm_0.8Sr_0.2NiO_2.