Preparation and characterization of a kind of physical crosslinking chitosan-poloxamer membrane containing nano-silver
Yunrui HU,Daheng LI,Jia CHEN,Xuefei YU,Tingfei XI,Xiaomei LUO,Kun CHEN
DOI: https://doi.org/10.3969/j.issn.1001-9731.2017.11.001
2017-01-01
Abstract:In order to prepare a kind of membrane which has a certain antibacterial property,well flexibility and good water absorption capacity,in this study,such a kind of membrane was prepared by the method of adj us-ting pH value of chitosan-poloxamer sol which were dissolved in dilute acetic acid solution.Membrane had been prepared by physical crosslinking method.Mechanical test,SEM test of the membranes'cross-section,absorp-tive capability and inhibition zone test had been carried out to test membrane's properties.The test results showed that the tensile strength and the elongation at break of prepared membrane were related to the concen-tration of poloxamer and glycerol.In SEM test of the cross-sectional of chitosan-poloxamer membrane,it had been found that the addition of poloxamer will induce the appearance of holes and the maximum diameter of the hole was less than 10μm.In the water-absorbing ability test,it had been found that 4‰ and 6‰ poloxamer group and 2% glycerol group had better water absorption capacity in PBS solution,while 8‰ poloxamer group and 2% glycerol group had better water absorption capacity in physiological saline solution.In the zone of inhi-bition test,it had been found that prepared membranes with different concentrations of poloxamer essentially had obvious inhibition zone.Finally,by combining the above properties,the optimal concentration of poloxamer and glycerol was 6‰ and 2%,respectively.Due to the convenience of preparation,good flexibility,good water absorption capacity and effective antibacterial properties,chitosan-poloxamer membrane was expected to be ap-plied in the treatment of burns and purulent wound infections.