Abstract:The crystallization process of β zeolite has been investigated by using FT-IR, XRD, TG, SEM, and ICP-AES. The samples were obtained by hydrothermal synthesis at 140 °C and chemical composition of the mixture used for synthesis can be expressed as n(Al2O3) : n(SiO2) : n(TEABr) : n (Na2O) : n(NaF) : n(H2O) : n [(NH4)2O] = 1 : 25 : 7. 5 : 2. 5 : 3. 75 : 550 : 6. 25. The crystallization curve of zeolite β exhibits a typical S-shaped characteristic. The typical framework IR-absorptions at 567 and 518 cm-1 have different natures. The former is detected at the beginning of induction period and its intensity changes a little in induction period, but exhibits a direct correlation with crystallinity in growth period. The latter is not detected in the induction period, but exhibits the same trend in growth period. The large amorphous SiO2-Al2O3 particles which are visible at the beginning of crystallization change into small grains during the induction period. n(SiO2)/n(Al2O3) ratio of the solid phases obtained at different synthesis time changes significantly during the induction period, but changes a little in growth period. So the β zeolite crystal nucleus are formed via liquid-phase synthesis mechanism. A typical gel in synthesis of β zeolite is transformed initially into a solid, which contains richer aluminium, minor F- and occluded TEA species. The aluminosilicate gel particles are dissolved by F- during the induction period and the transition complex, which has a specific weak X-ray diffraction peak at 2θ = 22. 8° and specific DTG pattern, is formed at the turning point from induction period to growth period. During the growth period Si and Al transport from the liquid to the solid phase at almost the same rates. F- anion has greater influence on the formation and turning of transition complex.

Synthesis and characterization of a novel intergrowth zeolite T-L

SYNTHESIS AND CHARACTERIZATION OF A-TYPE ZEOLITE MEMBRANES ON ALUMINA PARTICLES SURFACE

Synthesis and Characterization of High-Quality Zeolite LTA and FAU Single Nanocrystals

Intergrowth Zeolites, Synthesis, Characterization, and Catalysis

Intergrown New Zeolite Beta Polymorphs with Interconnected 12-Ring Channels Solved by Combining Electron Crystallography and Single-Crystal X-ray Diffraction

Direct Synthesis of Hierarchical LTA Zeolite Via a Low Crystallization and Growth Rate Technique in Presence of Cetyltrimethylammonium Bromide.

Zeolite Growth by Synergy Between Solution-Mediated and Solid-Phase Transformations

An Extra-Large Pore Zeolite Enabled by 1D-to-3D Topotactic Condensation

Synthesis, Surface and Crystal Structure Investigation of the Large Zeolite Beta Crystal

Synthesis of novel aluminoborosilicate isomorphous to zeolite TUN and its acidic and catalytic properties

Synthesis Route to Single-Walled Zeolite Nanotubes Enabled by Tetrabutylammonium Hydroxide

Synthesis and characterization of a novel framework zinc-substituted MFI zeolite

Intergrowth MFI Zeolite with Inverse Al Zoning and Predominant Sinusoidal Channels for Highly Selective Production of Styrene

Novel Mesoporous ZSM-5 Zeolite with Disparate Morphologies Synthesized by a Double Long-alkyl-chain Organosilane Template

Controllable and SDA-free synthesis of sub-micrometer sized zeolite ZSM-5. Part 1: Influence of alkalinity on the structural, particulate and chemical properties of the products

Kinetics Guided Synthesis and Performance of Monodisperse Zeolite LTA Microspheres

Interchain-expanded extra-large-pore zeolites

Synthesis of Extra-Large-Pore Zeolite ECNU-9 with Intersecting 14*12-Ring Channels

Synthesis and Characterization of A Stable Extra‐Large‐Pore Zeolite with 15×12×12 Member‐Ring Channels

A 3D extra-large-pore zeolite enabled by 1D-to-3D topotactic condensation of a chain silicate.

Synthesis of β Zeolite Using Tetraethylammonium Bromide Together with Fluoride as Composite of Template (II) - Studies on Crystallization Process of β Zeolite