Abstract:First, the ATRP initiator monosubstituted beta-CD-Br was successfully prepared, which was confirmed by H-1-NMR and MALDI-TOF. And then the water-soluble polymer (beta-CD-PDMAEMA) modified with beta-CD at the one end was synthesised by ATRP polymerization. The beta-CD-PDMAEMA and PF-ADA can form watersoluble nanoparticle (PF-NP) via the host-guest inclusion complexation between beta-CD and adamantane (ADA) as driving force. Dynamic light scattering (DLS) was employed to measure the effect of weight ratio of beta-CD-PDMAEMA/PF-ADA on R-h and PDI of PF-NP. The DLS results show that the weight ratio of beta-CD-PDMAEMA/PF-ADA with 4:1 could form smaller nanoparticle, the R-h is 119 nm. As well as four diffent self assembly methods impact on character of nanoparticles were also focused, while fixing the weight ratio of beta-CD-PDMAEMA/PF-ADA at 4 1. When 4 mL water was slowly injected into 1 mL THE solution of beta-CDPDMAEMA and PF-ADA under ultrasonication, the R-h of nanoparticle is equal to 81 nm. Transmission electron microscopy (TEM) and atomic force microscopy (AFM) were used to exam the morphology of nanoparticles. The results from TEM and AFM show that the nanoparticles are spherical with diameter of 100 nm, which is smaller than the results observed from DLS measuements. It is well-known that PDMAEMA chains exhibit a coil-to-globule transition above their lower critical solution temperature (LCST) in water solution. At last, the R-h of nanoparticles decreases with temperature increase. All these results show that the nanoparticles have the PF polymer as the core, with diameter of 100 nm and the PDMAEMA polymer as the shell with thick ness of 30 nm.

A Kind of Water-Soluble Polyfluorene Nanoparticles Prepared by Inclusion Complexation of Beta-Cyclodextrin