Amidoxime-Modified Polyacrylonitrile Nanofibers and Application to Cr (vi) Ions Adsorption

Bin Wang,Fan Zhang,Jiao-na Wang,Xiu-yan Li,Cong-ju Li

DOI: https://doi.org/10.11777/j.issn1000-3304.2016.15365

2016-01-01

Acta Polymerica Sinica

Abstract:The electrospun polyacrylonitrile (PAN) nanofibers were chemically modified with amidoxime groups by reacting with hydroxylamine hydrochloride into amidoxime-modified PAN (AOPAN). SEM, FTIR and water contact angle test were used to characterize its physicochemical properties, and then AOPAN was applied for Cr(VI) ions adsorption. The results show that AOPAN nanofibers swelled and bended to a certain degree after hydro-thermal treatment at 60 degrees C for 3. 5 h. In the FTIR spectra, the double peaks at 3500 - 3300 cm(-1) are ascribed to the typical - NH2 absorption peak. And the water contact angle decreased from 114.5 degrees to 29.8 degrees. It suggests that the AOPAN nanofibers were obtained through this method. The Cr(VI) adsorption test shows that the adsorption capacity of AOPAN nanofibers is as high as 102.5 mg/g at pH = 2 and the adsorption equilibrium can be quickly reached within 5 h. This is mainly due to the protonation of -NH2 groups under the acid condition, which is benefit for adsorbing HCrO4-. Moreover the AOPAN nanofibers maintained over 50% removal rate after rinsing with dilute NaOH solution by four cycles. Thus, these AOPAN nanofibers have a high recyclable ability and are promising in heavy metal ions adsorption.