Synthesis of Phosphazene Derivative Modified alpha-Zirconium Phosphate and Its Effect on the Flame Retardancy and Mechanical Properties of Silicone Rubber in Combination with Ammonium Polyphosphate

Yong Ding,Yuan-fang Luo,Feng Xue,Zhi-xin Jia,De-min Jia
DOI: https://doi.org/10.11777/j.issn1000-3304.2017.17005
2017-01-01
Acta Polymerica Sinica
Abstract:A novel functionalized alpha-zirconium phosphate (F-ZrP) was synthesized by phosphazene derivative via in situ intercalation, modified by dicyandiamide (DICY), and then combined with hexachlorocyclotriphosphazene (HCCP) through nucleophilic substitution and further reacted with excessive DICY. Flame retardant silicone rubber composites (FRSR) were prepared via incorporation of F-ZrP and ammonium polyphosphate (APP) with silicone rubber by mechanical blending. The structure of F-ZrP and its morphology in silicone rubber were tested by X-ray diffraction (XRD), transmission electronic microscopy (TEM), thermogravimetric analysis (TGA), Fourier transform infrared spectroscopy (FTIR) and scanning electronic microscopy (SEM). The results show that the interlayer spacing of F-ZrP was larger compared with that of alpha-ZrP and phosphazene derivative efficiently combined with alpha-ZrP. F-ZrP existed with a structure of the intercalated components in FRSR. The effect of F-ZrP on the thermal stability and flame retardancy of FRSR in combination with APP was studied by TGA, vertical burning test (UL-94), limiting oxygen index (LOI) and Cone calorimeter test. TGA results illustrated that an optimal F-ZrP content could improve the thermal stability and char residue. The addition of F-ZrP to FRSR increased the LOI value and enhanced the UL-94 rating. When the total content of the flame retardants was 20 phr and the mass ratio of F-ZrP to APP was 1: 19, LOI value of FRSR was increased from 30.0 to 31.4, UL-94 rating was enhanced to V-0, and the peak heat release rate was 265.3 kW/m(2). The morphology and structure of the char residue were characterized by SEM. The results suggested that the combination of F-ZrP and APP could make the char residue more stable, compact, and continuous, delaying therefore the volatilization of the decomposition product and inhibiting underlying FRSR from contacting heat and oxygen. These results indicated that there was a synergistic flame retardancy effect in gas phase and condensed phase between F-ZrP and APP for FRSR. Moreover, the mechanical properties could be reinforced with an appropriate content of F-ZrP.
What problem does this paper attempt to address?