Hollow Silica and Ps@ Silica Microspheres with Their Respective Surfaces Being Modified with Au or Ag Nanoparticles and Their Performance As Sers Substrates

Jiao-jiao Wu,Sai-zhen Yao,Dao-yong Chen

DOI: https://doi.org/10.11777/j.issn1000-3304.2014.14108

2014-01-01

Acta Polymerica Sinica

Abstract:Polystyrene @ silica hybrid microspheres (PS @ SiO2) and hollow spheres of SiO2 (HSSi) were prepared using positively charged polystyrene (PS) microspheres as the template. Then, gold nanoparticles (Au-NPs) and silver nanoparticles (Ag-NPs) were modified onto the surface of PS @ SiO2 and HSSi, respectively,through the bridging coupling by mercapto silane coupling agents,which leads to the following four kinds of composite microspheres with uniform structures and narrow size distributions: (1) HSSi with the surface being modified with Au-NPs (HSSi-AuNPs); (2) PS@ SiO2 with the surface being modified with AuNPs (PS@ SiO2-AuNPs); (3) HSSi with the surface being modified with Ag-NPs (HSSi-AgNPs) and (4) PS@ SiO2 with the surface being modified with AgNPs (PS @ SiO2-AgNPs). These composite microspheres were used as SERS substrates, whose sensitivity, reproducibility and stability were evaluated by using crystal violet (CV) as the probe. The detection limits of CV by HSSi-AuNPs, PS@ SiO2-AuNPs,HSSi-AgNPs and PS @ SiO2-AgNPs are 10(-10) mol/L,10(-9) mol/L,10(-11) mol/L and 10(-11) mol/L, respectively. All these substrates exhibit relatively high sensitivities; the hollow structures make positive contributions to the sensitivities. Results of repeated Raman measurements of CV on the different spots randomly selected from the substrates confirm that all the substrates have good reproducibility. Moreover, all the substrates have a good stability, because they still have good sensitivities after having been stored in ambient environment for 3 months.