Abstract:N,N-Di-hydroxyethyl amine-3-propionic acid methyl ester was prepared in a nitrogen atmosphere. And SiO2-HBP-L was in situ synthesized by grafting from with the monomers and alpha-caprolactone. The structure and morphology were characterized by FTIR, XPS and TG analysis. The results show that the hyperbranched polyester is successfully grafted at the surface of nano-SiO2. Compared with the nano-SiO2, the SEM shows that the dispersion and compatibility of SiO2-HBP-L in the ethanol and rubber matrix is better. Then SiO2-HBP-L/SBR composites were prepared by using the direct mixing method. Vulcanization performance tests show that the curing time (T-90) of the composites are much shorter and the composites' total crosslinking density is increased with respect to SiO2/SBR composites. When the composites with 30 phr SiO2-HBP-L, the T-90 was reduced to 3.30 min. What is more, SiO2-HBP-L/SBR composites have a great improvement of mechanical properties and wear resistance. It shows that the tensile strength, elongation at break, tear strength and wear resistance of the composites are increasing with the increase of contents of SiO2-HBP-L. The tensile strength, elongation at break of the composites with 30 phr SiO2-HBP-L were 14.8 MPa and 22.2 kN/m(2), and its wear resistance decreased to 289.4 mm(3). Nano-SiO2 modified with long-subchain hyperbranched polyester (SiO2-HBP-L) was used in the preparation of SiO2-HBP-USBR composites. The results show that the performance of SiO2-HBP-L is better than that of nano-SiO2 in the reinforcement of SBR.

Preparation of Hyperbranched Polyester Modified Nano-Sio2 and Its Application in Sbr