Abstract:Copoly(arylene ether nitrile ketone)s bearing phthalazinone moiety (PPENKs) were successfully synthesized by the nucleophilic substitution reaction of 4-(4-hydroxylphenyl)-2,3-phthalazin-1(2 H )-one (DHPZ), a new bisphenol-like monomer with twisted non-coplanar structure, with various molar proportions of 2,6-dichlorobenzonitrile (DCBN) to 4,4′-difluoro benzophenone (DFK) as coreactants in sulfolane at the present of anhydrous potassium carbonate. In order to obtain high-molecular weight polymers, DHPZ firstly polymerized with low-reactive DCBN for a given time at polymerization temperature after removal of water produced during the reaction, followed by addition of high-reactive DFK to continue the reaction until high-molecular weight polymers were obtained. These obtained copolymers had inherent viscosities between 0.45 and 0.80 dL/g in chloroform at a concentration of 0.5 g dL −1 at 25 °C, and their number-average molecular weights were in the ranges from 2.2 × 10 4 to 4.7 × 10 4 with the polydispersity of 2.05–2.70. The structure of typical PPENK5050 was ambiguously confirmed by FT-IR and 1 H-NMR. All of the PPENKs were amorphous and soluble in dipolar aprotic solvents, involving N -methyl pyrrolidione, N , N -dimethylacetamide, and chloroform at room temperature. The resulting copolymers showed glass transition temperatures ( T g s) between 267 and 287 °C, and the T g values of the copolymers were found to increase with increasing DCBN unit content in the polymer. Thermogravimetric studies showed that all of the polymers had 5 % weight loss temperatures ranging from 501 to 511 °C in nitrogen atmosphere. All of the PPENKs could be cast into transparent, strong, and flexible films. They displayed electrical surface resistivity of 10 13 Ω, indicating their potential application in electronic field. Physical properties of PPENK5050, which exhibited the best mechanical properties, were measured according to ASTM plastic standards. The results indicated that PPENK5050 possessed excellent thermal properties with the heat deformation temperature of 270 °C, which was 100 °C higher than PEN™ invented and commercialized by Idemitsu Kosan Company Limited. Its dielectric coefficient was 3.45 with the dielectric loss of 0.004 detected at 1 MHz. The other properties of PPENK5050 were equivalent to PEN™. They could be the promising materials as high-performance matrix in the application of polymer matrix composite, high-performance coating, adhesive, and membrane.

SYNTHESIS AND CHARACTERIZATION OF PHTHALAZINONE-CONTAINING POLY(ARYL ETHER NITRILE KETONE KETONE)S

Synthesis of poly(arylene ether nitrile ketone)s bearing phthalazinone moiety and their properties

Synthesis and properties of aromatic phthalazinone-containing poly(aryl ether nitrile ketone)s and its application in insulating coatings

Synthesis of Phthalazinone-containing Poly(aryl-ether-ketone) Block Copolymers with Good Solubility and High Thermal Stability

SYNTHESIS AND CHARACTERIZATION OF POLY (ETHER SULFONE KETONE KETONE) CONTAINING PHTHALAZINONE MOIETY

Synthesis and characterization of a novel phthalazinone poly(aryl ether sulfone ketone) with carboxyl group

Synthesis And Characterization Of Phthalazinone Poly(Aryl Ether Sulfone Ketone) With Carbonyl Group

Synthesis, Characterization, and Crosslinking of Soluble Cyano-Containing Poly(Arylene Ether)S Bearing Phthalazinone Moiety

Synthesis and Characterization of Phthalazinone‐based Poly(aryl Ether Ketone) Derived from 4,4′‐Dichlorobenzophenone

Synthesis, Characterization and Thermal Decomposition of Novel Soluble Copoly(aryl Ether Nitrile) Containing Phthalazinone and Biphenyl Moieties

Synthesis and Properties of Poly(phthalazinone Ether Ketone Ketone)s Containing Pendent Methyl Groups

SYNTHESIS AND PROPERTIES OF POLY(PHTHALAZINONE ETHER SULFONE KETONE)S FROM 4,4′-DICHLOROBENZOPHENONE

STUDY ON THE POLY(ARYL ETHER KETONE) CONTAINING PHTHALAZINONE AND NAPHTHALENE MOIETIES

Synthesis and Characterization of Poly （aryl Ether Ketone） Containing Phthalazinone and Naphthalene Moieties

Preparation and Properties of Film Materials of Poly(aryl Ether Ketone)-Based Phthalonitrile Resins

THE RELATIONSHIP OF STRUCTURE AND PROPERTY OF COPOLY (PHTHALAZINONE ETHER NITRILE PHENYL-1 , 3, 5-TRIAZINE) S

SYNTHESIS AND PROPERTIES OF POLY(ARYL KETONE) CONTAINING BIS(PHTHALAZINONE) AND METHYLENE MOIETIES

Synthesis and properties of organic soluble semicrystalline poly(aryl ether ketone)s copolymers containing phthalazinone moieties

SYNTHESIS AND PERFORMANCE OF NOVEL POLY (ARYL ETHERS) CONTAINING CHLORO -SUBSTITUTED PHTHALAZINONE MOIETIES

Synthesis and Properties of Phthalonitrile Terminated Polyaryl Ether Nitrile Containing Fluorene Group

Synthesis and Characterization of New Soluble Poly(aryl Ether Nitrile)s Containing Phthalazinone Moiety