Effect of Solvents on the Solution State and Film Condensed State Structures of a Polyfluorene Conjugated Polymer in the Dynamic Evolution Process from Solution to Film
Hao Zhang,Tao Li,Tengning Ma,Bin Liu,Jiaxuan Ren,Jinyi Lin,Mengna Yu,Linghai Xie,Dan Lu
DOI: https://doi.org/10.1021/acs.jpcc.9b07288
2019-01-01
The Journal of Physical Chemistry C
Abstract:Although much progress has been made in basic research on conjugated polymers and their practical applications in optoelectronic devices, so far research on the solution state, especially on the effect of solvent on conjugated polymers solution state and films condensed state structure in the dynamic evolution process from solution to film, is scarce. In this research, we focused on a special polyfluorene conjugated polymer, poly(9-(4-(octyloxy)phenyl)-2,7-fluoren-9-ol) (PPFOH), hydrogen bonding with supramolecular conjugated polymers in which intermolecular hydrogen bonds could be formed with different solvents, to explore the effect of solvents on PPFOH's solution state and the film's condensed state structure in the dynamic evolution process from solution to film. Dynamic/static light scattering, giving shape parameters and fractal dimension, UV-vis absorption spectra, photoluminescence spectra, transmission electron microscopy were used for this research. It was found that chain aggregation size, shape, and aggregated density presented obvious differences in PPFOH solutions with different solvents. Chain aggregation size was obviously increased in PPFOH chloroform (CF)/tetrahydrofuran (THF) mixed solution with different THF ratios, such as 0% THF (pure CF solvent), with CF/20% THF mixed solvent, and 100% THF solvent. A stretched and rigid chain conformation with dense chain aggregation was present in pure CF solvent, and there was a small number of fine lattice fringes with spacing 0.229 nm and an irregular crystalline appearance with the CF solvent. Although the ordered structures region was increased in the aggregation of PPFOH CF/THF mixed solution with 20% THF, the direction was cluttered with increased lattice fringe spacing of 0.252 nm. However, a large-area and long-range ordered chain aggregation was present in the PPFOH mixed solution with 100% THF solvent, with lattice fringes spacing 0.596 nm, quite high chain aggregation order, and high consistent lattice fringe direction. Interchain interaction between PPFOH chains or between PPFOH chains and solvents molecules (CF or THF) led to the difference in chain aggregate state structure in the PPFOH solution state. More importantly, it was found that there was heredity of the chain condensed state structure from solution to films in CF solvent in the dynamic evolution process due to strong intermolecular hydrogen-bonding interactions between PPFOH molecules in solution state and film. However, the influence of solvent on the film condensed state structure was limited because of solvent evaporation in the filming process, thus leading to enhancement of interchain interactions between PPFOH chains in all solvents. The condensed state structure of the final film was mainly decided by interactions of PPFOH chain itself but no solvents. Therefore, a rule for deciding chain aggregated state structure heredity from solution to film was revealed, that is, whether the intermolecular forces in both the solution and film are the same. If the intermolecular forces between PPFOH chains are the same, the chain aggregated state structure from solution to film is inherited; if they are different, the aggregated state structure from solution to film is not inherited. The research indicates intermolecular hydrogen bonds plays an important role in determining the effect of solvents from the solution state to the film; this is significant not only to reveal the effect of solvent on conjugated polymer solution behavior and film condensed state structure but also to deeply understand the physics of condensed state structure formation in the dynamic evolution process from solution to film in order to control the conjugated polymer condensed state structure to achieve photoelectric devices with high efficiency and stability.