Mechanically Robust and Recyclable Styrene–Butadiene Rubber Cross-Linked Via Cu2+–Nitrogen Coordination Bond after a Tetrazine Click Reaction
Qiang Wang,Wenchang Wang,Qiuying Li,Chifei Wu
DOI: https://doi.org/10.1021/acs.iecr.0c05249
2021-01-01
Industrial & Engineering Chemistry Research
Abstract:A metal-ligand complex is a useful noncovalent bond to build up a cross-link network. Unfortunately, it is a challenge to construct the coordination cross-link networks in commercial elastomers without ligand groups on their polymer chains. In this study, first, a tetrazine click reaction using 3,6-di(2-pyridyl)-1,2,4,5-tetrazine (DPT) successfully introduced nitrogen-containing groups into styrene-butadiene rubber (SBR) polymer chains with a facile process in the solid status. Then, the introduced groups on SBR could further coordinate with Cu2+ after mixing with CuSO4 and heating under pressure in bulk. Differential scanning calorimetry, Fourier-transform infrared spectroscopy, H-1 NMR, X-ray photoelectron spectroscopy, and thermogravimetric analysis proved the modification of SBR by DPT, as well as the coordination between ligand groups on SBR and CuSO4. Elastic torque curves effectively monitored the formation of coordination cross-link networks. Finally, due to the reversible breaking and re-forming nature of metal-ligand bonds, the coordination cross-linked SBR exhibited high strength and toughness. Tensile strength up to 10.52 MPa at a fracture elongation of 695% was obtained when the designed DPT click reaction degree is 2% and the content of CuSO4 is 10 phr. The corresponding composite exhibited some recycling value, and the related fracture energy could sustain 58.9 and 30.7% compared to the virgin sample after being reprocessed once and three times, respectively. Thus, in this work, a simple approach was developed to convert widely used SBR into mechanically robust materials via metal-ligand bonds with some reprocessing and recycling ability without using any conventional vulcanizing agent and accelerator.