Abstract:We developed a synthetic method for amphiphilic and highly branched block copolymers composed of polystyrene and poly(N-isopropylacrylamide) (PNIPAM) through copolymerization of an anionic inimer (synthesized from monoaddition of 1,3-bis(1-phenylvinyl) benzene (MDDPE) with s-butyllithium) and styrene, followed by mechanism transformation from living anionic to controlled radical polymerization based on reversible addition-fragmentation chain transfer process. The mechanism transformation was achieved on the basis of conversion of living anionic species into thiocarbonylthio moieties by sequential reaction with CS2 and 1-phenylethyl bromide, affording a dendritic chain transfer agent (Dendritic-CTA). The resulting Dendritic-CTA was further employed to mediate RAFT polymerization of NIPAM to give amphiphilic and highly branched block copolymer. A series of amphiphilic and highly branched block copolymers were thus prepared by changing the feed ratio of NIPAM to Dendritic-CTA. The successful formation of Dendritic-CTA was confirmed by ultraviolet spectrum (UV), the structures of the Dendritic-CTA and the highly branched amphiphilic block copolymers were further characterized by H-1 nuclear magnetic resonance (H-1-NMR), gel permeation chromatography (GPC) equipped with multiangle laser light scattering detector. The solution properties of the highly branched amphiphilic block copolymers were investigated by fluorescence emission spectra (using nile red as the fluorescent probe), dynamic light scattering (DLS), and transmission electron microscopy (TEM). The fluorescence results show that the amphiphilic highly branched polymers have a low critical aggregation concentration (CAC) around 0.0035 mg/mL, and a temperature dependent multistage aggregation of the products in water was observed in the test of DLS. The DLS results also showed that the amphiphilic and highly branched block copolymers could form micelles with R-h size of 135 nm in water; the TEM results further illustrated that the amphiphilic and highly branched products could form spherical micelles and the diameters of the micelles were around 40 nm. Furthermore, the ability of the amphiphilic and highly branched products to stabilize the emulsion was studied using different oil/water systems. The results indicated a strong ability of emulsification arising from highly branched topology. Reversible formation of W/O and O/W was also observed due to the presence of PNIPAM segment with lower critical solution temperature (LCST). In addition, the emulsifying properties of the amphiphilic and highly branched products were closely dependent on the polarity of the solvents which were use to dissolved the polymers initially. The process may serve as a versatile approach to make amphiphilic and highly branched block copolymers with temperature responsiveness.

Tri-block Terpolymers with Different Sequences Synthesized by Combination of Anionic and RAFT Polymerizations

One-pot Synthesis of Octablock Copolymers of High-Molecular Weight Via RAFT Emulsion Polymerization

A Bifunctional Β-Diiminate Zinc Catalyst with CO2/Epoxides Copolymerization and RAFT Polymerization Capacities for Versatile Block Copolymers Construction

Polystyrene-<i>block</i>-poly(<i>n</i>-butyl acrylate)-<i>block</i>-polystyrene Triblock Copolymer Thermoplastic Elastomer Synthesized via RAFT Emulsion Polymerization

The Synthesis of High Molecular Weight Block Copolymers by Raft Polymerization

Synthesis and Characterization of Amphiphilic Triblock Copolymers with Identical Compositions but Different Block Sequences

Synthesis of Amphiphilic ABC Triblock Copolymers by Single Electron Transfer Nitroxide Radical Coupling Reaction in Tetrahydrofuran

Direct transformation of living anionic polymerization into RAFT-based polymerization

Synthesis of Well-defined Poly(tetrahydrofuran)-b-Poly(a-amino Acid)s Via Cationic Ring-opening Polymerization (ROP) of Tetrahydrofuran and Nucleophilic ROP of N-thiocarboxyanhydrides

Synthesis of (Hard-Soft-hard)x Multiblock Copolymers Via RAFT Emulsion Polymerization and Mechanical Enhancement Via Block Architectures

One‐pot Synthesis of Well‐defined Multiblock Polymer: Combination of ATRP and RAFT Polymerization Involving Cyclic Trithiocarbonate

Synthesis and Self-Assembly of Amphiphilic ABA Type Triblock Copolymer with Well-Defined Glycopolymer Segments

Synthesis of Amphiphilic Highly Branched Block Copolymers Based on Mechanism Transformation from Anionic Polymerization into RAFT-based Polymerization

Telechelic Triblock Poly(α‐Amino Acid)‐Poly(Tetrahydrofuran)‐Poly(α‐Amino Acid) Copolymers: Chain‐End Transformation, Polymerization and Ph‐responsive Hydrolysis†

Synthesis of Triblock Copolymer Having Alternating Structures and Kinetics Study on Raft-Mediated Bulk, Miniemulsion and Seed Miniemulsion Polymerizations

A Facile Synthesis of Cleavable Block Copolymers Via Tandem Polymerizations of NMRP and ATRP

Synthesis of Ps-B-Ppoa-B-Ps Triblock Copolymer Via Sequential Free Radical Polymerization and Atrp

Preparation of well-defined block copolymer having one polystyrene segment and another poly(styrene-alt-maleic anhydride) segment with RAFT polymerization

Synthesis of Block Copolymers Via the Combination of Raft and A Macromolecular Azo Coupling Reaction

Synthesis of a Novel ABC Triblock Copolymer with a Rigid-Rod Block via Atom Transfer Radical Polymerization

Atom transfer radical polymerization of PS-PHB-PS triblock copolymers