Dissolution Mechanism and Solution Properties of Natural Polysaccharides
Sen Wang,Rong-rong Zhang,Xiao-juan Xu,Ang Lu,Li-na Zhang
DOI: https://doi.org/10.11777/j.issn1000-3304.2017.17108
2017-01-01
Acta Polymerica Sinica
Abstract:Naturalpolymers such as cellulose, chitin, chitosan and other fungi polysaccharides are derived from renewable resources, which is one kind of main chemical raw materials in the future. The numerous intermolecular and intramolecular hydrogen bonds have made their dissolution difficult in most common solvents. Moreover, their structures are very complex. Clarifying their chain conformation and solution properties is essential in designing their molecular structure, realizing more sophisticated applications. This article introduces the recent results about low temperature dissolution of cellulose, chitin and chitosanin in alkali/urea aqueous solution and their chain conformation and solution properties, as well as solution properties of the active polysaccharides. Cellulose can be dissolved in 7 wt% NaOH-12 wt% urea aqueous solution with precooling (-12 degrees C) within 2 min, whereas chitin can be dissolved in a mixture of NaOH, urea and water atweight ratio of 11:4:85 at -30 degrees C. The weight average molecular weight (M-w), radii of gyration (< R-g >(z)), hydrodynamic radii (< R-h >(z)), the structure-sensitive parameter (rho) and persistent length (q) values of the natural macromolecules were determined, indicating the worm-like stiff chain conformation of cellulose, chitin and chitosan. Furthermore, TEM, cryo-TEM and AFM images provide direct observation of the extended chain conformation and the visualized nanofibers constructed from the stiff chains in parallel aggregation in the aqueous solution. A water-soluble neutral polysaccharide (AF1) was extracted from A. auricula-judae was and identified as a high branched beta-(1 -> 3)-D-glucan. AF1 was proved to exist as stiff chains in water, and as flexible chains in dimethylsulfoxide (DMSO). The high-branched glucan was used to self-assemble into hollow nanofibers with apparent average diameter of 92 nm. Lentinan, a beta-(1 -> 3)-D-glucan isolated from Lentinus edodes, exhibited good water solubility, and existed as a triple-helical conformation in the aqueous solution at 25 degrees C. AFM images confirmed that the triple-helical chain conformation of lentinan with high M-w formed wormlike patterns in aqueous solution at 25 degrees C. Water-insoluble polysaccharide (TM3a), extracted from sclerotia of Pleurotus tuber-regium, was identified as ahyperbranched beta-D-glucan. The degree of branching of TM3a was 65.5%. The dependence of intrinsic viscosity ([eta]), radius of gyration (< S-2 > z(1/2)), and hydradynamic radius (R-h) on the weight-average molecular weight (M-w) was studied, indicating that TM3a existed as a compact chain conformation with a sphere-like structure in LiCl/DMSO solution. Furthermore, TEM image provided direct observation of the sphere-like pattern of the chain conformation.