Synthesis and Characterization of Optically Active Poly {(+)-2,5-bis[4 '-((S)-(2-methylbutoxyphenyl)]benzyl Methacrylate}

Cui Jiaxi,Cao Hongqing,Liu Anhua,Wan Xinhua
DOI: https://doi.org/10.3321/j.issn:1000-3304.2009.10.011
2009-01-01
Acta Polymerica Sinica
Abstract:A chiral vinyl monomer, ( +)-2,5-bis [4'-((S)-(2-methylbutoxyphenyl)]benzyl methacrylate, was synthesized and polymerized via both conventional radical polymerization and atom transfer radical polymerization The monomer showed a specific optical rotation [alpha](365)(25) (c = 0.2 g/dL) of 59.5 degrees in THF, while the corresponding polymer displayed its I a 136,25 value less than that of monomer for about 30 degrees. In the UV-Vis absorption regions of ester and p-terphenyl side-groups, the monomer exhibited very weak Cotton effects. In a sharp contrast., the polymer gave negative and positive Cotton effects centered at 302 and 270 nm, respectively. These results suggested the formation of a chiral secondary structure of polymer backbone, the optical rotation of which was opposite to that of monomer. For a vinyl polymer like poly 1( +)-2, 5-bis [ 4'-( ( S M 2-methylbutoxyphenyl I benzyl niethacrylate I (PBPBMA) the most possible chiral structure was helical conformation of main-chain with an excess helix sense. The reaction temperature and solvent were varied to study the effect of polymerization condition on the [ a 1 25 value Of the POIVInCr. It was found that the a Value of the polymer was independent on the polymerization conditions employed. The specific optical rotations of polymers decreased with increasing molecular weight at beginning and then leveled off, consistent with the speculation of helical conformation generation. The content of min dyads of PBPBMA was Only about 10% US estimated with H-1-NMR by converting the polymer to poly( methyl methacrylate) PMMA which was comparable to that of PMMA obtained via conventional radical polymerization This might account for the lower optical activity of PBPBMA compared to that of poly I ( +) -2, 5 his E 4'- S) -2-methylboutyloxy)phenyl]styrene] an optically active helical vinyl polymer with similar structure
What problem does this paper attempt to address?