Poly(vinyl Alcohol) Nanocrystal-Assisted Hydrogels with High Toughness and Elastic Modulus for Three-Dimensional Printing

Ang Li,Yi Si,Xiaohan Wang,Xianjing Jia,Xuhong Guo,Yisheng Xu

DOI: https://doi.org/10.1021/acsanm.8b01786

IF: 6.14

2019-01-01

ACS Applied Nano Materials

Abstract:Flexibility, diversity, and applicability in complicated situations are urgently required for next generation of tough hydrogels with good processability. To achieve this good performance, complicated chemical polymerization is conventionally involved in the preparation of tough hydrogels, which is tedious, energy-consuming, detrimental to the environment, and hard to scale up. In contrast, physically cross-linking primarily the electrostatic force is always adopted as complementary to chemical crosslinking. Here we propose a simple, nonpolymerization method to develop a novel type of dual physically cross-linked tough hydrogel, which consists of poly(vinyl alcohol) (PVA) crystallite cross-linked network, and hyaluronic acid-Fe3+ physically cross-linked network. Instead of using electrostatic interaction, nanosized PVA crystallites were chosen as major cross-linking sites for the primary network of the hydrogel. By annealing the freeze-thaw hydrogel followed by the Fe3+-carboxylic group complexation to construct the second network, extraordinary mechanical performance including excellent tensile strength (similar to 8 MPa), remarkable toughness (similar to 19.6 MJ/m(3)) and high elastic modulus (similar to 10MPa) was successfully achieved. Especially, the precursor solution with viscoelastic properties was demonstrated to as a "new" type of ink for three-dimensional (3D) printing with no UV curing is required. Such design provides a simple and new avenue for the preparation of tough hydrogels featured with 3D printing processability and we believe that the design can be potentially applied for building future soft devices.