Abstract:A solvothermal method was used to synthesize functionalized graphene, which exhibits an ultrahigh capacitance. This solvothermal method allows a fine control of the density of functionalities on graphene surface. The structure of resulting functionalized graphene is characterized by X-ray photoelectron spectroscopy (XPS), thermal gravimetric analysis (TGA), FTIR and Raman. Pseudocapacitance is provided by functionalities on graphene surface, such as carboxyl, carbonyl and hydroxyl. The significance of these functional also includes improving the wetting properties of electrode material, especially for supercapacitors using aqueous electrolyte. However, there is a penalty for functionalities since these oxygen-containing functional groups will disrupt the π-conjugated system and lower the electrical conductivity. Therefore for functionalized graphene as supercapacitor, a tradeoff exists between the high psudeocapacitance and low conductivity, both are arising from the surface functionalities. Our systematic study shows a successful control of the density of functionalities, which is essential to achieve high performance of graphene-based supercapacitors. The capacitance of graphene is measured in a three electrode system using cyclic voltammetry (CV) and galvanostatic charging/discharging techniques. At a proper reduction condition, a high capacity of 276 F/g was achieved at a discharging current of 0.1 A/g in H <sub xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">2</sub> SO <sub xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">4</sub> solutions. The superior capacitive performance of functionalized graphene demonstrates the importance of surface property engineering, which will greatly promote the study and application of graphene-based supercapacitors.

Production of Few-Layer Graphene Via Enhanced High-Pressure Shear Exfoliation in Liquid for Supercapacitor Applications

Sprinkling MnFe2O4 Quantum Dots on Nitrogen-Doped Graphene Sheets: the Formation Mechanism and Application for High-Performance Supercapacitor Electrodes

Optimized Supercapacitive Performance of Graphene-Hydrogel by Porous Texture Controlling

Electrospray-Deposition of Graphene Electrodes: A Simple Technique to Build High-Performance Supercapacitors

Simultaneous Electrochemical Exfoliation and Chemical Functionalization of Graphene for Supercapacitor Electrodes

One-Step Scalable Fabrication of Nitrogen and Chlorine Co-doped Graphene by Electrochemical Exfoliation for High-Performance Supercapacitors

A High-Performance, Low Defected, and Binder-Free Graphene-Based Supercapacitor Obtained via Synergistic Electrochemical Exfoliation and Electrophoretic Deposition Process

High-throughput Fabrication of Strutted Graphene by Ammonium-Assisted Chemical Blowing for High-Performance Supercapacitors

Substrate Engineered Interconnected Graphene Electrodes with Ultrahigh Energy and Power Densities for Energy Storage Applications

Surface engineering of graphene for high performance supercapacitors

Large-Area Fabrication of Porous Graphene Networks on Carbon Fabric via Millisecond Photothermal Processing of Polyaniline for Supercapacitors

Few-layer graphene production through graphite exfoliation in pressurized CO 2 assisted by natural surfactant

High-Performance Supercapacitors Based on Graphene/Activated Carbon Hybrid Electrodes Prepared Via Dry Processing

Scalable Self-Propagating High-Temperature Synthesis Of Graphene For Supercapacitors With Superior Power Density And Cyclic Stability

Mass Production of Graphene Nanoscrolls and Their Application in High Rate Performance Supercapacitors.

Use of Few-Layer Graphene Synthesized under Conditions of Self-Propagating High-Temperature Synthesis for Supercapacitors Applications

High-concentration shear-exfoliated colloidal dispersion of surfactant–polymer-stabilized few-layer graphene sheets

Wet-spun, porous, orientational graphene hydrogel films for high-performance supercapacitor electrodes.

Co/Mg Self-Propagating Combustion Synthesis of Few-Layer Graphene for Supercapacitors

Formation of a CoMn-Layered Double Hydroxide/Graphite Supercapacitor by a Single Electrochemical Step

Powder, paper and foam of few-layer graphene prepared in high yield by electrochemical intercalation exfoliation of expanded graphite.