Hierarchical Structure Formation and Effect Mechanism of Ni/Mn Layered Double Hydroxides Microspheres with Large-Scale Production for Flexible Asymmetric Supercapacitors

Tie Li,Jian Wang,Yan Xu,Yudong Cao,Hongzhen Lin,Ting Zhang

DOI: https://doi.org/10.1021/acsaem.8b00321

IF: 6.4

2018-01-01

ACS Applied Energy Materials

Abstract:In this study, Ni/Mn layered double hydroxides (LDHs) microspheres with three-dimensional flower-like hierarchical structure are fabricated by a large-scale and self-assembled chemical coprecipitation strategy (at 55 degrees C under normal pressure). In each integrated microsphere, the petals consist of ultrathin two-dimensional nanosheets. The self-assembly formation mechanism of this flower-like construction is systematically investigated according to the analysis results from the regulation of various reaction factors. The Ni/Mn LDHs microspheres show an optimal capacitance value as high as 1379 F.g(-1) at 1 A.g(-1). Sum frequency generation spectroscopy and charge storage behavior mechanism analysis further demonstrate that a favorable capacitive constitution is indeed dependent on the synergistic effect of active sites (different feed ratios) and surface area (different architectural features). Moreover, a novel flexible all-solid-state asymmetric supercapacitor is assembled by exploiting these microspheres and active carbon as positive and negative electrode materials respectively, which exhibits a superior capacitance value of 393 F.g(-1) (1 A.g(-1)) and energy and power density of 131.17 Wh.kg(-1) and 1.45 KW.kg(-1) with favorable cyclic life (remains over 75.1% after 5000 cycles under 50 mV.s(-1)), respectively. Overall, this work provides a significant prospect and deep understanding for the development of the next generation of flexible energy devices.