Abstract:Magnetic nanoparticles (MNPs) modified simultaneously with amorphous Fe and Mn oxides (Mag-Fe-Mn) were synthesized to remove arsenite [As(III)] from water. Mag-Fe-Mn particles were fabricated through heterogeneous nucleation technique by employing the maghemite as the magnetic core and Fe Mn binary oxide (FMBO) as the coating materials. Powder X-ray diffraction, X-ray photoelectron spectroscopy (XPS), Raman spectroscopy, and transmission electron microscopy were utilized to characterize the hybrid material. With a saturation magnetization of 23.2 emu/g, Mag-Fe-Mn particles with size of 20 -50 nm could be easily separated from solutions with a simple magnetic process in short time (within 5 min). At pH 7.0, 200 mu g/L of As(III) could be easily decreased to below 10 mu g/L by Mag-Fe-Mn particles (0.1 g/L) within 20 min. As(III) could be effectively removed by Mag-Fe-Mn particles at initial pH range from 4 to 8 and the residual As was completely oxidized to less toxic arsenate [As(V)]. The co-occurring redox reactions between Mn oxide and As(III) was confirmed by XPS analysis. Chloride, sulfate, bicarbonate, and nitrate at common concentration range had negligible influence on As(III) removal, whereas, silicate and phosphate reduced the As(III) removal by competing with arsenic species for adsorption sites. As(M) removal was not obviously affected by natural organic matter (up to 8 mg/L as TOC). Mag-Fe-Mn could be regenerated with ternary solution of NaOH, NaCl, and NaClO. Throughout five consecutive cycles, the adsorption and desorption efficiencies maintained above 98% and 87%, respectively. Mag-Fe-Mn had a larger adsorption capacity for As(III) (47.76 mg/g) and could remove trace As(III) more thoroughly than MNPs modified solely with either Fe or Mn oxide due to the synergistic effect of the coating Fe and Mn oxides. This research extended the potential applicability of FMBO to a great extent and provided a convenient approach to efficiently remove trace As(III) from water. (C) 2013 Elsevier Ltd. All rights reserved.

Selective Removal of High Concentration Arsenate from Aqueous Solution by Magnetic Fe–Y Binary Oxide

Arsenic removal from aqueous solutions by adsorption onto iron oxide/activated carbon magnetic composite

Magnetic Mesoporous TiO2 Microspheres for Sustainable Arsenate Removal from Acidic Environments

Removal of Arsenic Contaminants with Magnetic Γ-Fe2o3 Nanoparticles

Adsorption of organic and inorganic arsenic from aqueous solution: Optimization, characterization and performance of Fe–Mn–Zr ternary magnetic sorbent

Efficient Removal of As(III) Via Simultaneous Oxidation and Adsorption by Magnetic Sulfur-Doped Fe-Cu-Y Trimetal Oxide Nanoparticles

[Arsenic Adsorption by Magnetic Adsorbent CuFe2O4].

Removal of arsenate by cetyltrimethylammonium bromide modified magnetic nanoparticles.

Enhanced As (V) Removal from Aqueous Solution by Biochar Prepared from Iron-Impregnated Corn Straw

Enhanced removal of trace arsenate by magnetic nanoparticles modified with arginine and lysine

Removal of As(V) from aqueous solution using modified Fe3O4 nanoparticles

Magnetic Zeolitic Imidazolate Frameworks Composite As an Efficient Adsorbent for Arsenic Removal from Aqueous Solution.

Preparation and Evaluation of a Novel Fe–Mn Binary Oxide Adsorbent for Effective Arsenite Removal

Selective and Efficient Removal of As(V) and As(III) from Water by Resin-Based Hydrated Iron Oxide

Preparation of Fe-Mn bimetal oxide adsorbent and its adsorption characteristics of arsenic

Rapid and selective removal of trace As(III) from water using Fe Mn binary oxide

Construction of magnetic bimetallic oxide‐decorated attapulgite‐based adsorbents for arsenic ion adsorption

Efficient Removal of Trace Arsenite Through Oxidation and Adsorption by Magnetic Nanoparticles Modified with Fe-Mn Binary Oxide

Adsorption behavior and mechanism of different arsenic species on mesoporous MnFe 2 O 4 magnetic nanoparticles.

One-Step Preparation of Chitosan-Based Magnetic Adsorbent and Its Application to the Adsorption of Inorganic Arsenic in Water

Adsorption Behavior and Mechanism of Arsenic on Mesoporous Silica Modified by Iron-Manganese Binary Oxide (Femnox/sba-15) from Aqueous Systems.