Chemical Reaction Kinetics and the Characteristic Properties of Injectable Adhesives of Nano-Hydroxyapatite/ag3po4/polyurethane for Bone and Tooth Repair

Quanjing Mei,Lili Lin,Jian Wang,Bin Cai,Qin Zou,Jidong Li,Yubao Li,Yi Zuo

DOI: https://doi.org/10.1007/s42452-019-0707-x

2019-01-01

Abstract:Advancements have been made to injectable polymer technologies following the development of minimally invasive techniques for bone and tooth treatment. To improve the conversion rate and avoid potential toxicity of traditional injectable polymer, new injectable adhesives have been developed to ensure good biocompatibility, while optimizing their suitable mechanical and antibacterial properties. In this study, we synthesized a two-part injectable n-HA/Ag 3 PO 4 /polyurethane system (PU) featuring different contents of nanohydroxyapatite (n-HA) and silver salt (Ag 3 PO 4 ). After the prepolymer (Part A) mixed with a hardener (Part B), the compounded adhesive was injected into pores and set in situ with antibacterial properties. The results indicated that a high conversion rate reached 95% within 24 h could effectively reduce the release of a toxic monomer. Among these composites, the incorporation of n-HA in PU was the critical factor to ensure the adhesive’s material characteristics and cytocompatibility. With the increased content of n-HA, from 0 to 30 wt%, the compressive strength, setting time, surface wettability, and differentiation activities improved significantly. Although the injectability and setting time of the PUs decreased with the increase of n-HA, the values of injectable PUs still met with ISO standard requirements. The antibacterial tests against Staphylococcus aureus showed that the incorporation of Ag 3 PO 4 in PUs (1 wt% and 3 wt%) exhibited stronger antimicrobial effects than that without the addition of silver. Compared to the PUs with the addition of 3 wt% Ag 3 PO 4 , which led to poor cellular viability, PUs with 1 wt% Ag 3 PO 4 not only offered good antimicrobial properties, but also expressed excellent cytocompatibility, suggesting that this agent might be a promising injectable adhesive system.