Abstract:A particle size dependence for CO oxidation over rhodium nanoparticles of 1.9-11.3 nm has been investigated and determined to be modified by the existence of the capping agent poly(vinylpyrrolidone) (PVP). The particles were prepared using a polyol reduction procedure with PVP as the capping agent. The Rh nanoparticles were subsequently supported on SBA-15 during hydrothermal synthesis to produce Rh/SBA-15 supported catalysts for size-dependent catalytic studies. CO oxidation by O-2 at 40 Torr CO and 100 Torr O-2 was investigated over two series of Rh/SBA-15 catalysts: as-synthesized Rh/SBA-15 covering the full range of Rh sizes and the same set of catalysts after high temperature calcination and reduction. The turnover frequency at 443 K increases from 0.4 to 1.7 s(-1) as the particle size decreases from 11.3 to 1.9 nm for the as-synthesized catalysts. After calcination and reduction, the turnover frequency is between 0.1 and 0.4 s(-1) with no particle size dependence. The apparent activation energy for all catalysts is similar to 30 kcal mol(-1) and is independent of particle size and thermal treatment. Infrared spectroscopy of CO on the Rh nanoparticles indicates that the heat treatments used influence the mode of CO adsorption. As a result, the particle size dependence for CO oxidation is altered after calcination and reduction of the catalysts. CO adsorbs at two distinct bridge sites on as-synthesized Rh/SBA-15, attributable to metallic Rh(0) and oxidized Rh(I) bridge sites. After calcination and reduction, however, CO adsorbs only at Rh(0) atop sites. The change in adsorption geometry and oxidation activity may be attributable to the interaction between PVP and the Rh surface. This capping agent affect may open new possibilities for the tailoring of metal catalysts using solution nanoparticle synthesis methods.

NbOPO4 Supported Rh Nanoparticles with Strong Metal-Support Interactions for Selective CO2 Hydrogenation.

Product Selectivity Controlled by Nanoporous Environments in Zeolite Crystals Enveloping Rhodium Nanoparticle Catalysts for CO2 Hydrogenation

Adsorbate-mediated strong metal–support interactions in oxide-supported Rh catalysts

Overturning CO2 Hydrogenation Selectivity with High Activity Via Reaction-Induced Strong Metal-Support Interactions.

Overturning CO<sub>2</sub> Hydrogenation Selectivity with High Activity via Reaction-Induced Strong Metal–Support Interactions

Overturning CO 2 Hydrogenation Selectivity with High Activity via Reaction-Induced Strong Metal–Support Interactions

Colloidally Synthesized Monodisperse Rh Nanoparticles Supported on SBA-15 for Size- and Pretreatment-Dependent Studies of CO Oxidation

Facilitated CO2 Hydrogenation by Strong Metal-Support Interaction Between Ni and BaCO3

CO2 Methanation on Supported Rh Nanoparticles: The combined Effect of Support Oxygen Storage Capacity and Rh Particle Size

Grain Boundaries Modulating Active Sites in RhCo Porous Nanospheres for Efficient CO2 Hydrogenation

Supported Rhodium Oxide Nanoparticles As Highly Active CO Oxidation Catalysts

Selective Hydrogenation of CO2 to Ethanol over Sodium-Modified Rhodium Nanoparticles Embedded in Zeolite Silicalite-1

Strong Metal-Support Interaction Promoted Via Constructing Biocarbon Membrane for Enhanced CO Preferential Oxidation Activity of Rh/CaCO3@biocarbon

Enhanced CO2 Methanation Activity of Ni/Anatase Catalyst by Tuning Strong Metal–Support Interactions

Reduction‐induced metal/oxide interfacial sites for selective CO2 hydrogenation

Insights into Structure and Dynamics of (Mn,fe)ox-Promoted Rh Nanoparticles

Strong Metal–Support Interactions Between Nickel and Iron Oxide During CO2 Hydrogenation

Support effect on Ni-based mono- and bimetallic catalysts in CO2 hydrogenation

Hydroxyl-mediated Ethanol Selectivity of CO2 Hydrogenation.

Tuning the CO2 Hydrogenation Activity Via Regulating the Strong Metal–Support Interactions of the Ni/Sm2O3 Catalyst

Insight into the Metal‐Support Interactions Between Ruthenium and Nanodiamond‐derived Carbon Material for CO Oxidation