Hypercrosslinked aromatic heterocyclic microporous polymers

Bien Tan,Yali Luo,Buyi Li,Wei Wang,Kangbing Wu

DOI: https://doi.org/10.21558/sos-2015-0002

2015-01-01

Sample of Science

Abstract:Aromatic heterocyclic microporous polymers with high surface areas are obtained by directly crosslinking the heterocyclic monomers under mild conditions. Owing...

What problem does this paper attempt to address?

Hypercrosslinked aromatic heterocyclic microporous polymers: a new class of highly selective CO2 capturing materials.

Yali Luo,Buyi Li,Wei Wang,Kangbing Wu,Bien Tan

DOI: https://doi.org/10.1002/adma.201202447

IF: 29.4

2012-01-01

Advanced Materials

Abstract:Aromatic heterocyclic microporous polymers with high surface areas are obtained by directly crosslinking of the heterocyclic monomers under mild conditions. Owing to the narrow pore system and the heteroatom-rich pore surface, these networks exhibit high CO2 adsorption capacity and selectivity. At 273 K, the CO2/N-2 selectivity of Py-1 is about 117, which is among the highest the reported microporous materials.
Heterocyclic Microporous Polymers: Hypercrosslinked Aromatic Heterocyclic Microporous Polymers: A New Class of Highly Selective CO2 Capturing Materials (adv. Mater. 42/2012)

Yali Luo,Buyi Li,Wei Wang,Kangbing Wu,Bien Tan

DOI: https://doi.org/10.1002/adma.201290260

IF: 29.4

2012-01-01

Advanced Materials

Abstract:On page 5703, Bien Tan and co-workers demonstrate an easy and straightforward route for the preparation of aromatic heterocycle-based microporous organic polymers. Owing to the narrow pore system and the heteroatom-rich pore surface, these networks exhibit large CO2 adsorption capacity and high selectivity toward CO2/N2. The frontispiece shows the density map of the adsorbed CO2 molecules in the simulated microporous structure.
Knitting hypercrosslinked conjugated microporous polymers with external crosslinker

liangxiao tan,buyi li,xinjia yang,weixing wang,bien tan

DOI: https://doi.org/10.1016/j.polymer.2015.06.026

IF: 4.6

2015-01-01

Polymer

Abstract:A new series of hypercrosslinked polymers were efficiently synthesized by knitting rigid aromatic building blocks using a novel external crosslinker (1,4-dimethoxybenzene, DMB) which result in a conjugated microporous structure. This knitting hypercrosslinked conjugated microporous polymers (HCCMPs) are predominantly microporous and exhibit high surface area of up to 800 m2 g−1, which also show comparable gas uptake properties reaching 1.14 wt. % H2 adsorption at 1.13 bar/77 K, and 12.72 wt. % CO2 adsorption at 1.13 bar/273 K, respectively. The extended π-conjugated structure and the three-dimensional network of π–π stacked aryl rings enable these HCCMPs good luminescence properties and high electrical conductivity.
Research Progress in Hypercrosslinked Microporous Organic Polymers

Tan Liangxiao,Tan Bien

DOI: https://doi.org/10.6023/a15020096

2015-01-01

Acta Chimica Sinica

Abstract:Hypercrosslinked microporous polymers are currently an important class of porous polymer materials and receiving great interest due to their advantages such as high surface area, moderate synthetic conditions and diverse building blocks. According to the difference between the synthetic methods, hypercrosslinked polymers are mainly prepared by the following three strategies: polymer precursor post-crosslinking, one-step self-polycondensation of multifunctional monomers and external crosslinker knitting rigid aromatic compounds. In this review, we introduce the development of hypercrosslinked polymer in detail as well as investigate various synthetic methods and polymer networks with controlled micro-morphology, the broad practical and potential applications including gas storage, adsorption, separation and heterogeneous catalysis were also discussed. In the end, we talk about the disadvantage of hypercrosslinked polymers and challenges in the future as well as predict the further development on synthesis and application.
A New Strategy to Microporous Polymers: Knitting Rigid Aromatic Building Blocks by External Cross-Linker

Buyi Li,Ruini Gong,Wei Wang,Xin Huang,Wang Zhang,Huanmin Li,Chunxiao Hu,Bien Tan

DOI: https://doi.org/10.1021/ma200630s

IF: 5.5

2011-01-01

Macromolecules

Abstract:A series of microporous polymers has been obtained via a low-cost versatile strategy, which involves "knitting" rigid aromatic building blocks, such as benzene, biphenyl, 1,3,5-triphenylbenzene, methylbenzene, chlorobenzene, and phenol using an external cross-linker. These materials are predominantly microporous and exhibit high surface areas. Moreover, different building blocks can generate materials with different pore structures, functional groups and application properties, which are significant: for materials design.
Microporous organic polymers synthesized by self-condensation of aromatic hydroxymethyl monomers

Yali Luo,Shoucun Zhang,Yunxiang Ma,Wei Wang,Bien Tan

DOI: https://doi.org/10.1039/c2py20914d

IF: 4.6

2013-01-01

Polymer Chemistry

Abstract:Two hypercross-linked polymer networks have been synthesized by the self-condensation of bishydroxymethyl monomer, 1,4-benzenedimethanol (BDM), and monohydroxymethyl compound, benzyl alcohol (BA). This is different from the previous reports where multifunctional monomers or cross-linkers are crucial for constructing the porous polymer networks. N-2 sorption isotherms for the polymers show that both materials are predominantly microporous with Brunauer-Emmett-Teller (BET) surface areas of 847 m(2) g(-1) for HCP-BDM and 742 m(2) g(-1) for HCP-BA. A network based on BA can also store a significant amount of CO2 (8.46 wt%) and H-2 (0.97 wt%) at 1.0 bar, and at 273 K and 77 K respectively, despite its relatively modest surface area. Based on these results, this study opens up the possibility of synthesizing porous materials using monofunctional monomers.
Recent development of hypercrosslinked microporous organic polymers.

Shujun Xu,Yali Luo,Bien Tan

DOI: https://doi.org/10.1002/marc.201200788

IF: 5.006

2013-01-01

Macromolecular Rapid Communications

Abstract:Hypercrosslinked polymers (HCPs) are currently receiving great interest due to their easy preparation, high chemical and thermal stability, and low cost. Combined with the lightweight properties and high surface areas HCPs can be considered as promising materials for gas storage and separation, catalysis, and heavy metal ions removal in wastewater treatment. This Feature Article summarizes strategies for the preparation of HCPs, comprising the post-crosslinking of Davankov-type resins, direct polycondensation of aromatic chloromethyl (or hydroxymethyl) monomers, and knitting aromatic compound polymers (KAPs). The HCPs applications, such as H2 storage, CO2 capture, and heterogeneous catalysis, are also discussed throughout in the article. Finally, the outlook of this research area is given.
Hypercrosslinked porous polymer materials: design, synthesis, and applications

Liangxiao Tan,Bien Tan

DOI: https://doi.org/10.1039/c6cs00851h

IF: 46.2

2017-01-01

Chemical Society Reviews

Abstract:Hypercrosslinked polymers (HCPs) are a series of permanent microporous polymer materials initially reported by Davankov, and have received an increasing level of research interest. In recent years, HCPs have experienced rapid growth due to their remarkable advantages such as diverse synthetic methods, easy functionalization, high surface area, low cost reagents and mild operating conditions. Judicious selection of monomers, appropriate length crosslinkers and optimized reaction conditions yielded a well-developed polymer framework with an adjusted porous topology. Post fabrication of the as developed network facilitates the incorporation of various chemical functionalities that may lead to interesting properties and enhance the selection toward a specific application. To date, numerous HCPs have been prepared by post-crosslinking polystyrene-based precursors, one-step self-polycondensation or external crosslinking strategies. The advent of these methodologies has prompted researchers to construct well-defined porous polymer networks with customized micromorphology and functionalities. In this review, we describe not only the basic synthetic principles and strategies of HCPs, but also the advancements in the structural and morphological study as well as the frontiers of potential applications in energy and environmental fields such as gas storage, carbon capture, removal of pollutants, molecular separation, catalysis, drug delivery, sensing etc.
Unprecedented Processable Hypercrosslinked Polymers with Controlled Knitting.

Shaolei Wang,Chengxin Zhang,Qingsong Liu,Bien Tan

DOI: https://doi.org/10.1002/marc.202100449

IF: 5.006

2021-01-01

Macromolecular Rapid Communications

Abstract:Processable microporous organic polymers (MOPs) attract incomparable research interest because their vairous types, such as monoliths and membranes are for practical application. Most processable MOPs usually need harsh conditions such as the use of expensive metal catalysts, specialized stereospecific monomers, etc., which restrict the sustainable and real applications of processable MOPs. Therefore, the economical mass production of processable MOPs remains a formidable challenge. Herein, a novel strategy is reported for constructing processable hypercrosslinked polymers (HCPs) need two steps synthesis of pre-crosslinking and deep-crosslinking using divinylbenzene (DVB) as a self-crosslinking monomer under the catalysis of a small amount of FeCl3. The resulting HCPs monoliths possess high BET surface area of 1033-1056 m(2) g(-1) with hierarchical porosity, and show excellent mechanical strength up to 65 MPa. It is, to the best of authors' knowledge, the first report of using aromatic vinyl monomers as self-crosslinking monomers to generate HCPs monoliths with high surface area, yielding no by-products, and high mechanical strength.
A N-heterocyclics Induced Π-Π Interaction Strategy to Synthesis Hyper-Crosslinked Polymers with Enhanced Porosity for Xenon Adsorption

Jialin Wang,Lijie Mi,Meng He,Yingzhe Du,Xiangdong Ding,Jianhui Lan,Weiqun Shi,Xue Liu

DOI: https://doi.org/10.1016/j.seppur.2024.130157

IF: 8.6

2025-01-01

Separation and Purification Technology

Abstract:Hyper-crosslinked polymers (HCPs) with large specific surface areas play an important role in gas adsorption and separation. However, the method to enhance the specific surface area of HCPs and gas adsorption performance without changing the polyaromatic hydrocarbons (PAHs) monomer structure and reaction condition is still missing. Here, we present a general and facile N-heterocyclics induced pi-pi interaction strategy to increase the specific surface area of HCPs by simply adding N-heterocyclics during the Friedel-Crafts alkylation reaction. The specific surface areas of HCP (tetraphenylmethane based HCPs, TPMBPy-TCM) increased up to 7.78 times compared to the one without adding N-heterocyclics. The crosslinking and stacking of PAHs was influenced by the pi-pi stacking between the N-heterocyclic complexes and PAHs. More importantly, N-heterocyclics coordinated with Lewis acids have lower electron density and do not react with PAHs in the Friedel-Crafts alkylation reaction, which can be removed easily from HCPs. The HCPs obtained shown good xenon adsorption performance with Xe uptake of 3.63 mmol/g, which is the highest value for organic adsorbents reported in literature. This work provides new insight into the preparation of high-performance HCPs.
Chapter 4. Recent Developments of Hypercrosslinked Microporous Organic Polymers

Liangxiao Tan,Bien Tan

DOI: https://doi.org/10.1039/9781782622260-00066

2015-01-01

Abstract:This chapter seeks to bring the readers, in a very brief way, the strategies for the preparation of hypercrosslinked microporous organic polymers comprising the post-crosslinking of “Davankov-type” resins, direct polycondensation of functionalized (chloromethyl) aromatic monomers, and knitting aromatic compound with an external crosslinker. The applications, such as H2 storage, CO2 capture, and heterogeneous catalysis, as well as morphology control, are also discussed throughout the chapter.
Versatile Postmodification of Linear Poly-P-phenylene to Prepare Microporous Polymeric Networks Using the Double Aromatic Nucleophilic Substitution Reaction

Liming Tao,Junping Ju,Fang Niu,Tingmei Wang,Qihua Wang

DOI: https://doi.org/10.1016/j.polymer.2013.07.075

IF: 4.6

2013-01-01

Polymer

Abstract:Microporous, hypercrosslinked poly-p-phenylenes with surface area of up to 1735 m(2) g(-1) have been prepared by combination of super acid catalyzed polymerization and the double aromatic nucleophilic substitution reaction. The surface area and pore size can be controlled by varying the amount of the crosslinking reagents, which tuned the crosslinking degree effectively. The capacity of adsorption of CO2 of the MPNs largely depends on their specific surface areas. (c) 2013 Elsevier Ltd. All rights reserved.
Effects of synthesis methodology on microporous organic hyper-cross-linked polymers with respect to structural porosity, gas uptake performance and fluorescence properties

Shuangshuang Hou,Shumaila Razzaque,Bien Tan

DOI: https://doi.org/10.1039/c8py01730a

IF: 4.6

2019-01-01

Polymer Chemistry

Abstract:The structural characteristics of hyper-cross-linked polymers (HCPs) make them interesting for a wide variety of applications. To form knitted HCPs various synthesis approaches including solvent knitting, a knitting method using formaldehyde dimethyl acetal (FDA) as an external cross-linker and the Scholl coupling reaction have been used. However, a systematic study of these strategies has not been explored. Here HCPs have been made using facile synthesis methodologies and characterized to reveal resulting Brunauer-Emmett-Teller (BET) surface areas up to 2278 m(2) g(-1) and 2064 m(2) g(-1) with CO2 adsorption capacities of 20.89 wt% and 18.95 wt% (at 273.15 K/1.00 bar), respectively. Detailed information is also given with respect to distinctions in textural properties, gas uptake performances and optical properties. More importantly, our comparative studies have revealed the significance and efficiency of solvent knitting when used to fabricate HCP materials with good porosities and gas uptake abilities. Among these approaches, the knitting method with FDA as an external cross-linker is the most time-efficient technique, whereas the Scholl coupling reaction has advantages for the production of fluorescent polymers. Based on the proposed mechanisms, changes in structural features can also be rationally explained.
The Review and Introduction of Hypercrosslinked Polymer

Tariq Shah,Yanting Lyu,Baoliang Zhang

DOI: https://doi.org/10.1016/b978-0-323-99039-4.00003-6

2023-01-01

Abstract:Hypercrosslinked polymers (HCPs) are a kind of nanoporous material having a wide application, including gas sorption and separation, heterogeneous catalysis, drug delivery, and chromatographic separation. HCPs, which were first invented by Davankov and Tsyurupa in the early 1970s, have grown in popularity over the last few decades. Moderate synthesis conditions, a vast stockroom of affordable monomers, sturdy structures, and high thermal and chemical stabilities are only a few of the benefits of HCPs materials. This chapter mainly introduces the synthesis, properties, and applications of hypercrosslinked polymers. HCPs materials can be made by postcrosslinking polystyrene-type precursors in their swollen condition or by condensation of tiny building blocks, both of them are based on Friedel-Crafts chemistry and it provides fast kinetics which can form strong linkage producing highly crosslinked network with leading porosity. The various chemical modification reactions relevant to this area are also introduced. Several examples of applications for hypercrosslinked materials are described and grouped into thematic areas such as sensing, photocatalysis, drug delivery, gas separation, and removal of pollutants.
Postmodification of linear poly-p-phenylenes to prepare hyper-crosslinked polymers: Tuning the surface areas by the molecular weight

di zhang,liming tao,junping ju,yanming wang,qihua wang,tingmei wang

DOI: https://doi.org/10.1016/j.polymer.2015.01.053

IF: 4.6

2015-01-01

Polymer

Abstract:Microporous, hyper-crosslinked poly-p-phenylenes have been prepared by combination of superacid-catalyzed polymerization and then crosslinking with external crosslinkers, e.g. tetrachloromethane (CCl4) and dimethoxymethane (DMM). The porosity property can be tuned by changing the molecular weight of the linear poly-p-phenylenes. With the increase of linear polymer molecular weight, the surface areas increase fleetly and then decrease. The highest surface area is 1019 m2/g, for HCP-9-DMM. The effect of solvent amount on HCPs' surface area was also studied. Moreover, the CO2 storage capacity of these materials was tested, where HCP-9-DMM shows the highest CO2 adsorption capacity of 93 mg/g.
Hyper-Cross-Linked Phenolic Hydroxyl Polymers with Hierarchical Porosity and Their Efficient Adsorption Performance

You Wang,Yangqi Gan,Jianhan Huang

DOI: https://doi.org/10.1021/acs.iecr.9b06621

2020-01-01

Industrial & Engineering Chemistry Research

Abstract:Functionalized hyper-cross-linked polymers with a unique porosity were promising materials, while their facile fabrication remains a challenge. Herein, a novel synthetic strategy was developed based on two Friedel-Crafts alkylation reactions for chloromethylated polystyrene and the hyper-cross-linked phenolic hydroxyl polymers were successfully fabricated. The first lowtemperature reaction (at 313 K) offered the polymers plentiful phenolic hydroxyl and the second high-temperature reaction (at 358 K) provided the polymers with the hyper-cross-linking frameworks with a unique hierarchical porosity. Benefiting from the synthetic protocol, the resultant samples exhibited promising properties for aniline adsorption (q(max): 198.8 mg/g) and CO2 capture (105 mg.g(-1) at 273 K and 1 bar). Moreover, the hierarchical porosity facilitated the kinetic adsorption and about 90 min was enough to reach the equilibrium.
Hyper-Cross-Linked Organic Microporous Polymers Based on Alternating Copolymerization of Bismaleimide.

Hui Gao,Lei Ding,Wenqing Li,Guifeng Ma,Hua Bai,Lei Li

DOI: https://doi.org/10.1021/acsmacrolett.6b00015

IF: 5.8

2016-01-01

ACS Macro Letters

Abstract:A novel type of hyper-cross-linked organic microporous polymer (HOMP) has been successfully prepared based on the radical copolymerization of bismaleimides and divinylbenzene. In comparison with the HOMPs prepared with cross-linking techniques, the new radical strategy circumvents some intractable problems, such as low atom economy, structure irregularity and corrosive byproducts. The obtained HOMPs have defined molecular structures due to the intrinsic alternating copolymerization properties of the two monomers. A maximum BET surface area of 841 m2 g-1 and high gas capture capacity (CO2, 11.22 wt %, 273 K/1.0 bar; H2, 0.82 wt %, 77.3 K/1.0 bar; benzene, 545 mg g-1, room temperature/0.6 bar; and cyclohexane, 1736 mg g-1, room temperature/0.6 bar) were achieved. In addition, the polymers also displayed good chemical and thermal stability, which is critical for the practical application.
Hypercrosslinked polymers: controlled preparation and effective adsorption of aniline

Yin Liu,Xinlong Fan,Xiangkun Jia,Baoliang Zhang,Hepeng Zhang,Aibo Zhang,Qiuyu Zhang

DOI: https://doi.org/10.1007/s10853-016-0118-y

IF: 4.5

2016-01-01

Journal of Materials Science

Abstract:A series of microporous polymers was produced via the self-condensation of dichloroxylene which is a typical bischloromethyl monomer for a one-step synthetic process. The influences of experimental conditions including type of solvent, reaction time, and addition amount of catalyst on the polymer properties were systematically investigated. The results showed that Brunauer–Emmett–Teller (BET) specific surface areas and pore volumes of the hypercrosslinked polymers (HCPs) increased rapidly as the increase of reaction time at first and then remained nearly constant. In addition, there is a threshold concentration of catalyst for producing HCPs with high BET specific surface areas and big pore volumes. Under optimal reaction conditions, when 1, 2-dichloroethane was used as solvent, reaction time was 21 h and the molar ratio of catalyst to dichloroxylene was one; the microporous polymer with maximum BET specific surface area of up to 1446.32 m 2 /g was obtained. Furthermore, the adsorption performance of the as-prepared HCPs was studied using aniline as model adsorbate. The adsorption of aniline followed a pseudo-second-order model, and the adsorption isotherm was proved to fit the Langmuir adsorption model ( R 2 > 0.99). The maximum adsorption capacity of aniline could reach 769.23 mg/g at 20 °C.
Hypercrosslinked Polystyrene Microspheres with Bimodal Pore Size Distribution and Controllable Macroporosity

Qingquan Liu,Li Wang,Weiting Yu,Anguo Xiao,Haojie Yu,Jia Huo

DOI: https://doi.org/10.1002/app.31422

IF: 3

2010-01-01

Journal of Applied Polymer Science

Abstract:A combination Of Suspension polymerization and postcrosslinking was used to prepare hypercrosslinked polystyrene (H-PS) microspheres with controllably bimodal pc re size distribution in the presence of toluene and polypropylene (PP) as a coporogen. The proportion of PP in the coporogen was changed to investigate the influence of the coporogen composition on the pore structure of the H-PS microspheres. The addition of a small amount of PP achieved the aim of a clearly bimodal pore size distribution and the control of the macroporosity of the H-PS microspheres, which have potential application in the preparation of catalyst Supports. The specific surface area of the H-PS microspheres could be adjusted in the range 380-790 m(2)/g by changes in the concentration of FT in the coporogen. Moreover, the H-PS microspheres displayed all the characteristics of Davankov-type resins by their ability to be swollen in both thermodynamically poor solvents such as water and good solvents such as toluene. Finally, the possible mechanism of porosity formation during polymerization and postcrosslinking was also examined by a combination of pore structure data and the appearance of the microspheres before and after postcrosslinking. (C) 2009 Wiley Periodicals, Inc. J Appl Polym Sci 116: 84-92, 2010
Heteroaromatic Hyperbranched Polyelectrolytes: Multicomponent Polyannulation and Photodynamic Biopatterning

Xiaolin Liu,Minghui Xiao,Ke Xue,Mingzhao Li,Dongming Liu,Yong Wang,Xinzhe Yang,Yubing Hu,Ryan T. K. Kwok,Anjun Qin,Chunlei Zhu,Jacky W. Y. Lam,Ben Zhong Tang

DOI: https://doi.org/10.1002/anie.202104709

2021-01-01

Angewandte Chemie International Edition

Abstract:We reported an efficient multicomponent polyannulation for in situ generation of heteroaromatic hyperbranched polyelectrolytes by using readily accessible internal diynes and low-cost, commercially available arylnitriles, NaSbF6, and H2O/AcOH. The polymers were obtained in excellent yields (up to 99%) with extraordinary high molecular weights (M-w up to 1.011 x 10(6)) and low polydispersity indices. The resulting polymers showed good processibility and high quantum yields with tunable emission in the solid state, making them ideal materials for highly ordered fluorescent photopatterning. These hyperbranched polyelectrolytes also possessed strong ability to generate reactive oxygen species, which allowed their applications in efficient bacterial killing and customizable photodynamic patterning of living organisms in a simple and cost-effective way.

Hypercrosslinked aromatic heterocyclic microporous polymers

Hypercrosslinked aromatic heterocyclic microporous polymers: a new class of highly selective CO2 capturing materials.

Heterocyclic Microporous Polymers: Hypercrosslinked Aromatic Heterocyclic Microporous Polymers: A New Class of Highly Selective CO2 Capturing Materials (adv. Mater. 42/2012)

Knitting hypercrosslinked conjugated microporous polymers with external crosslinker

Research Progress in Hypercrosslinked Microporous Organic Polymers

A New Strategy to Microporous Polymers: Knitting Rigid Aromatic Building Blocks by External Cross-Linker

Microporous organic polymers synthesized by self-condensation of aromatic hydroxymethyl monomers

Recent development of hypercrosslinked microporous organic polymers.

Hypercrosslinked porous polymer materials: design, synthesis, and applications

Unprecedented Processable Hypercrosslinked Polymers with Controlled Knitting.

A N-heterocyclics Induced Π-Π Interaction Strategy to Synthesis Hyper-Crosslinked Polymers with Enhanced Porosity for Xenon Adsorption

Chapter 4. Recent Developments of Hypercrosslinked Microporous Organic Polymers

Versatile Postmodification of Linear Poly-P-phenylene to Prepare Microporous Polymeric Networks Using the Double Aromatic Nucleophilic Substitution Reaction

Effects of synthesis methodology on microporous organic hyper-cross-linked polymers with respect to structural porosity, gas uptake performance and fluorescence properties

The Review and Introduction of Hypercrosslinked Polymer

Postmodification of linear poly-p-phenylenes to prepare hyper-crosslinked polymers: Tuning the surface areas by the molecular weight

Hyper-Cross-Linked Phenolic Hydroxyl Polymers with Hierarchical Porosity and Their Efficient Adsorption Performance

Hyper-Cross-Linked Organic Microporous Polymers Based on Alternating Copolymerization of Bismaleimide.

Hypercrosslinked polymers: controlled preparation and effective adsorption of aniline

Hypercrosslinked Polystyrene Microspheres with Bimodal Pore Size Distribution and Controllable Macroporosity

Heteroaromatic Hyperbranched Polyelectrolytes: Multicomponent Polyannulation and Photodynamic Biopatterning